Metal-organic frameworks (MOFs) containing d0 metals such as NH2-MIL-125(Ti), NH2-UiO-66(Zr) and NH2-UiO-66(Hf) are among the most studied MOFs for photocatalytic applications. Despite structural similarities, we demonstrate that the electronic properties of these MOFs are markedly different. As revealed by quantum chemistry, EPR measurements and transient absorption spectroscopy, the highest occupied and lowest unoccupied orbitals of NH2-MIL-125(Ti) promote a long lived ligand-to-metal charge transfer upon photoexcitation, making this material suitable for photocatalytic applications. In contrast, in case of UiO materials, the d-orbitals of Zr and Hf, are too low in binding energy and thus cannot overlap with the π* orbital of the ligand, making both frontier orbitals localized at the organic linker. This electronic reconfiguration results in short exciton lifetimes and diminishes photocatalytic performance. These results highlight the importance of orbital contributions at the band edges and delineate future directions in the development of photo-active hybrid solids.

Recently, MIL-125(Ti) and NH2 -MIL-125(Ti), two titanium-based metal-organic frameworks, have attracted significant research attention in the field of photocatalysis for solar fuel generation. This work reveals that the differences between these structures are not only based on their light absorption range but also on the decay profile and topography of their excited states. In contrast to MIL-125(Ti), NH2 -MIL-125(Ti) shows markedly longer lifetimes of the charge-separated state, which improves photoconversion by the suppression of competing decay mechanisms. We used spectroelectrochemistry and ultrafast spectroscopy to demonstrate that upon photoexcitation in NH2 -MIL-125(Ti) the electron is located in the Ti-oxo clusters and the hole resides on the aminoterephthalate unit, specifically on the amino group. The results highlight the role of the amino group in NH2 -MIL-125(Ti), the electron donation of which extends the lifetime of the photoexcited state substantially.

The inclusion of Ti(IV) in water-stable metal-organic frameworks has been proposed as a strategy for the generation of high surface area heterogeneous photocatalysts, with UiO-66 being a promising candidate. We find that the site of binding of Ti(IV) is at linker defect sites and not incorporated into the inorganic secondary building unit through metal exchange. We also demonstrate the choice of titanium source is critical in the generation of an active hydrogen evolution catalyst, and explain the observed activity using density functional theory calculations, which also enable rational design of future Ti(IV) coordination environments in MOF catalysts.

The fascinating chemical and physical properties of MOFs have recently stimulated exploration of their application for photocatalysis. Despite the intense research effort, the efficiency of most photocatalytic MOFs for solar fuel generation is still very modest. In this highlight we analyse the current status of the field and stress the potential of advanced spectroscopic techniques to gain structural and mechanistic insight and hence support the future development of MOFs to harvest and store solar energy.

The Ti-containing metal organic framework (MOF) MIL-125 has been used as sacrificial precursor to obtain TiO2 materials through the MOF-mediated synthesis route. In this study, Fe 3+ was deposited on the surface of MIL-125 after its hydrothermal synthesis. Targeted Fe-doped titania photocatalysts were prepared through the direct calcination in air of Fe/MIL-125 crystals and/or by using a two-step method, including carbonization in inert atmosphere followed by calcination in air. The relationship between the synthesis conditions and the properties of the Fe-doped titania nanopowders, such as Fe content, porosity, phase composition and particle size was investigated.From elemental mapping, X-ray photoelectron spectroscopy, X-ray absorption spectroscopy, UV-Vis absorption spectroscopy and photoluminescence emission spectra, the presence of highly dispersed Fe 3+ ions incorporated into the TiO2 crystal lattice was confirmed, which led to a significant red shift of photoresponse towards visible light and reduced the recombination rate of electron-hole pairs at low iron content. By varying the pre-carbonization temperature, both crystal size and phase composition in the final materials were modulated. The performance of Fe-doped titania materials in photocatalytic water-splitting was tested for hydrogen evolution. Optimal photocatalytic performance was found at 0.15 and 0.5 wt. % iron concentration and exceeded those of non-doped titania and commercial anatase both under visible and UV light irradiation, respectively, and among the highest reported in literature for these systems.

Insight into the operation at the molecular level of a promising light-driven H2 production system based on Co catalytic sites hosted in a Ti-based MOF.

No abstract

No abstract