The evolution of precipitation and microstructure during a simulation of the thin slab direct rolling process, in six vanadium based, low carbon, steels with V, V-N, V-Ti-N, V-Nb, V-Nb-Ti and V-Zr additions was studied by optical microscopy, analytical transmission electron microscopy (TEM), energy dispersive X-ray analysis (EDAX) and parallel electron energy loss spectroscopy (PEELS). Tensile properties and Charpy vee-notch toughness of the final strip were also determined. The effects of microalloying additions and processing conditions, including equalisation temperature (1 200°C, 1 100°C and 1 050°C) and end water cool temperature, on the austenite and ferrite grain sizes, as well as the type and composition of the precipitates, were determined. The relationship between the microstructure and the properties in the steels was also ascertained.

A study has been undertaken of four vanadium based steels which have been processed by a simulated direct charging route using processing parameters typical of thin slab casting, where the cast product has a thickness of 50 to 80mm ( in this study 50 mm) and is fed directly to a furnace to equalise the microstructure prior to rolling. In the direct charging process, cooling rates are faster, equalisation times shorter and the amount of deformation introduced during rolling less than in conventional practice. Samples in this study were quenched after casting, after equalisation, after 4 th rolling pass and after coiling, to follow the evolution of microstructure. The mechanical and toughness properties and the microstructural features might be expected to differ from equivalent steels, which have undergone conventional processing. The four low carbon steels (~0.06wt%) which were studied contained 0.1wt%V (V-N), 0.1wt%V and 0.010wt%Ti (V-Ti), 0.1wt%V and 0.03wt%Nb (VNb), and 0.1wt%V, 0.03wt%Nb and 0.007wt%Ti (V-Nb-Ti). Steels V-N and V-Ti contained around 0.02wt% N, while the other two contained about 0.01wt%N. The as-cast steels were heated at three equalising temperatures of 1050°C, 1100°C or 1200°C and held for 30-60 minutes prior to rolling. Optical microscopy and analytical electron microscopy, including parallel electron energy loss spectroscopy (PEELS), were used to characterise the 2 precipitates. In the as-cast condition, dendrites and plates were found. Cuboid particles were seen at this stage in Steel V-Ti, but they appeared only in the other steels after equalization.In addition, in the final product of all the steels, fine particles were seen, but it was only in the two titanium steels that cruciform precipitates were present. PEELS analysis showed that the dendrites, plates, cuboids, cruciforms and fine precipitates were essentially nitrides. The two Ti steels had better toughness than the other steels but inferior lower yield stress values. This was thought to be, in part, due to the formation of cruciform precipitates in austenite, thereby removing nitrogen and the microalloying elements which would have been expected to precipitate in ferrite as dispersion hardening particles.Dr Li is now with Vanitec,

This version is available at https://strathprints.strath.ac.uk/5778/ Strathprints is designed to allow users to access the research output of the University of Strathclyde. Unless otherwise explicitly stated on the manuscript, Copyright © and Moral Rights for the papers on this site are retained by the individual authors and/or other copyright owners. Please check the manuscript for details of any other licences that may have been applied. You may not engage in further distribution of the material for any profitmaking activities or any commercial gain. You may freely distribute both the url (https://strathprints.strath.ac.uk/) and the content of this paper for research or private study, educational, or not-for-profit purposes without prior permission or charge.Any correspondence concerning this service should be sent to the Strathprints administrator: strathprints@strath.ac.ukThe Strathprints institutional repository (https://strathprints.strath.ac.uk) is a digital archive of University of Strathclyde research outputs. It has been developed to disseminate open access research outputs, expose data about those outputs, and enable the management and persistent access to Strathclyde's intellectual output.

The compositions of sub-15 nm particles in six related vanadium high strength low alloy steels, made by simulated thin slab direct charged casting, have been determined using electron energy loss spectroscopy (EELS). Such particles are considered to be responsible for dispersion hardening. For the first time, particles down to 4 nm in size have had their composition fully determined. In all the steels, the particles were nitrogen and vanadium rich and possibly slightly substoichiometric carbonitrides. Equilibrium thermodynamics predicted much higher carbon to metal atomic ratios than observed in all cases so that kinetics and mechanical deformation clearly control the precipitation process. Thus it is important to formulate the steel with this in mind.

Molecular beam epitaxy was employed for the growth of HgCdTe-based n-p + -n device structures on (211)B oriented CdZnTe substrates. The device structures were processed as mesa isolated diodes, and operated as back-to-back diodes for the simultaneous detection of two closely spaced sub-bands in the mid-wave infrared spectrum. The devices were characterized by R 0 A values in excess of 5 × 10 5 Ω cm 2 at 78K, at f/2 fov and quantum efficiencies greater than 70% in each band. Infrared imagery from a focal plane array with 128 × 128 pixels was acquired simultaneously from each band at temperatures between 77 to 180K, with no observable degradation in the image quality with increase in temperature.

No abstract

No abstract

No abstract