Waste scrap tyres were thermally decomposed at the temperature of 600 °C and heating rate of 10 °C·min−1. Decomposition was followed by the TG analysis. The resulting pyrolytic carbon black was chemically activated by a KOH solution at 800 °C. Activated and non-activated carbon black were investigated using high pressure thermogravimetry, where adsorption isotherms of N2, CO2, and cyclohexane were determined. Isotherms were determined over a wide range of pressure, 0.03–4.5 MPa for N2 and 0.03–2 MPa for CO2. In non-activated carbon black, for the same pressure and temperature, a five times greater gas uptake of CO2 than N2 was determined. Contrary to non-activated carbon black, activated carbon black showed improved textural properties with a well-developed irregular mesoporous-macroporous structure with a significant amount of micropores. The sorption capacity of pyrolytic carbon black was also increased by activation. The uptake of CO2 was three times and for cyclohexane ten times higher in activated carbon black than in the non-activated one. Specific surface areas evaluated from linearized forms of Langmuir isotherm and the BET isotherm revealed that for both methods, the values are comparable for non-activated carbon black measured by CO2 and for activated carbon black measured by cyclohexane. It was found out that the N2 sorption capacity of carbon black depends only on its specific surface area size, contrary to CO2 sorption capacity, which is affected by both the size of specific surface area and the nature of carbon black.
The food industry produces large amounts of solid and also liquid wastes. Different waste materials and their mixtures were pyrolysed in the laboratory pyrolysis unit to a fi nal temperature of 800°C with a 10 minute delay at the fi nal temperature. After the pyrolysis process of the selected wastes a mass balance of the resulting products, off-line analysis of the pyrolysis gas and evaluation of solid and liquid products were carried out. The highest concentration of methane, hydrogen and carbon monoxide were analyzed during the 4th gas sampling at a temperature of approx. 720-780°C. The concentration of hydrogen was measured in the range from 22 to 40 vol.%. The resulting iodine numbers of samples CHFO, DS, DSFW reach values that indicate the possibility of using them to produce the so-called "disposable sorbents" in wastewater treatment. The WC condensate can be directed to further processing and upgrading for energy use.
Ionic liquids are increasingly used for their superior properties. Four water-immiscible ionic liquids (butyltriethylammonium bis(trifluoromethylsulfonyl)imide, octyltriethylammonium bis(trifluoromethylsulfonyl)imide, dodecyltriethylammonium bis(trifluoromethylsulfonyl)imide, butyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide) and their water miscible precursors (bromides) were synthesized in a microwave reactor and by conventional heating. The best conditions for microwave-assisted synthesis concerning the yield and the purity of the product are proposed. The heating in the microwave reactor significantly shortened the reaction time. Biocide and ecotoxic effects of synthesized ionic liquids and their precursors were investigated. All tested compounds had at least a little effect on the growth or living of microorganisms (bacteria or mold). The precursor dodecyltriethylammonium bromide was found to be the strongest biocide, but posed a risk to the aquatic environment due to its relatively high EC50 value in the test with Vibrio fischeri. We assumed that apart from the alkyl chain length, the solubility in water, duration of action, or type of anion can influence the final biocide and ecotoxic effect.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.