The La2O3 and Al2O3/La2O3 layers were grown on 4H-SiC by atomic layer deposition (ALD) method. The electrical properties of La2O3 on 4H-SiC were examined using metal-insulator-semiconductor (MIS) structures of Pt/La2O3(18nm)/4H-SiC and Pt/Al2O3(10nm)/La2O3(5nm)/4H-SiC. For the Pt/La2O3(18nm)/4H-SiC structure, even though the leakage current density was slightly reduced after the rapid thermal annealing at 500 oC, accumulation capacitance was gradually increased with increasing bias voltage due to a high leakage current. On the other hand, since the leakage current in the accumulation regime was decreased for the Pt/Al2O3/La2O3/4H-SiC MIS structure owing to the capped Al2O3 layer, the capacitance was saturated. But the saturation capacitance was strongly dependent on frequency, indicating a leaky interfacial layer formed between the La2O3 and SiC during the fabrication process of Pt/Al2O3(10nm)/ La2O3(5nm)/ 4H-SiC structure.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.