Alumina incorporating nitrogen (aluminum oxynitride; AlON) for immunity against charge injection was grown on a AlGaN/GaN substrate through the repeated atomic layer deposition (ALD) of AlN layers and in situ oxidation in ozone (O 3 ) ambient under optimized conditions. The nitrogen distribution was uniform in the depth direction, the composition was controllable over a wide range (0.5-32%), and the thickness could be precisely controlled. Physical analysis based on synchrotron radiation X-ray photoelectron spectroscopy (SR-XPS) revealed that harmful intermixing at the insulator/AlGaN interface causing Ga out-diffusion in the gate stack was effectively suppressed by this method. AlON/AlGaN/GaN MOS capacitors were fabricated, and they had excellent electrical properties and immunity against electrical stressing as a result of the improved interface stability.
Using aluminum titanium oxide (AlTiO, an alloy of Al2O3 and TiO2) as a high-k gate insulator, we fabricated and investigated AlTiO/AlGaN/GaN metal-insulator-semiconductor heterojunction field-effect transistors. From current low-frequency noise (LFN) characterization, we find Lorentzian spectra near the threshold voltage, in addition to 1/f spectra for the well-above-threshold regime. The Lorentzian spectra are attributed to electron trapping/detrapping with two specific time constants, ∼25 ms and ∼3 ms, which are independent of the gate length and the gate voltage, corresponding to two trap level depths of 0.5–0.7 eV with a 0.06 eV difference in the AlTiO insulator. In addition, gate leakage currents are analyzed and attributed to the Poole-Frenkel mechanism due to traps in the AlTiO insulator, where the extracted trap level depth is consistent with the Lorentzian LFN.
The impacts of inserting ultrathin oxides into insulator/AlGaN interfaces on their electrical properties were investigated to develop advanced AlGaN/GaN metal-oxide-semiconductor (MOS) gate stacks. For this purpose, the initial thermal oxidation of AlGaN surfaces in oxygen ambient was systematically studied by synchrotron radiation X-ray photoelectron spectroscopy (SR-XPS) and atomic force microscopy (AFM). Our physical characterizations revealed that, when compared with GaN surfaces, aluminum addition promotes the initial oxidation of AlGaN surfaces at temperatures of around 400 °C, followed by smaller grain growth above 850 °C. Electrical measurements of AlGaN/GaN MOS capacitors also showed that, although excessive oxidation treatment of AlGaN surfaces over around 700 °C has an adverse effect, interface passivation with the initial oxidation of the AlGaN surfaces at temperatures ranging from 400 to 500 °C was proven to be beneficial for fabricating high-quality AlGaN/GaN MOS gate stacks.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.