We report on the performance improvement of ohmic contact by a premetallization annealing process after mesa-isolation in quaternary InAlGaN/ GaN high electron mobility transistors (HEMTs). By employing a premetallization annealing, the contact and specific contact resistances are improved from 0.31 Ω Á mm and 3.67 Â 10 À6 Ω cm 2 to 0.21 Ω mm and 1.63 Â 10 À6 Ω cm 2 , respectively. The angle-resolved X-ray photoelectron spectroscopy (AR-XPS) confirm the formation of nitrogen vacancies from the reduced atomic ratio of nitrogen and the binding energy shift of In3d 5/2 , Al2p 1/2 , and Ga2p 3/2 toward the higher energy after the pre-metallization annealing. Nitrogen vacancies that act as n-type dopants make the effective Schottky barrier thinner leading to the improved contact resistance. When the pre-metallization annealing process is employed to fabricate 200-nm-long gate HEMTs, the on-resistance and the maximum transconductance are improved from 1.7 Ω mm and 400 mS mm À1 to 1.0 Ω mm and 618 mS mm À1 , respectively.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.