The goal of this retrospective clinical study was to evaluate the behavior of Morse-taper indexed abutments by analyzing the marginal bone level (MBL) after at least 12 months of function. Patients rehabilitated with single ceramic crowns between May 2015 and December 2020 received single Morse-taper connection implants (DuoCone implant) with two-piece straight abutment baseT used for at least 12 months, presenting periapical radiograph immediately after crown installation were enrolled. The position of the rehabilitated tooth and arch (maxilla or mandible), crown installation period, implant dimensions, abutment transmucosal height, installation site (immediate implant placement or healed area), associated with bone regeneration, immediate provisionalization, and complications after installation of the final crown were analyzed. The initial and final MBL was evaluated by comparing the initial and final X-rays. The level of significance was α = 0.05. Seventy-five patients (49 women and 26 men) enrolled had a mean period of evaluation of 22.7 ± 6.2 months. Thirty-one implant-abutment (IA) sets had between 12–18 months, 34 between 19–24 months, and 44 between 25–33 months. Only one patient failed due to an abutment fracture after 25 months of function. Fifty-eight implants were placed in the maxilla (53.2%) and 51 in the mandible (46.8%). Seventy-four implants were installed in healed sites (67.9%), and 35 were in fresh socket sites (32.1%). Thirty-two out of these 35 implants placed in fresh sockets had the gap filled with bone graft particles. Twenty-six implants received immediate provisionalization. The average MBL was −0.67 ± 0.65 mm in mesial and −0.70 ± 0.63 mm in distal (p = 0.5072). The most important finding was the statistically significant difference comparing the values obtained for MBL between the abutments with different transmucosal height portions, which were better for abutments with heights greater than 2.5 mm. Regarding the abutments’ diameter, 58 had 3.5 mm (53.2%) and 51 had 4.5 mm (46.8%). There was no statistical difference between them, with the following means and standard deviation, respectively, −0.57 ± 0.53 mm (mesial) and −0.66 ± 0.50 mm (distal), and −0.78 ± 0.75 mm (mesial) and −0.746 ± 0.76 mm (distal). Regarding the implant dimensions, 24 implants were 3.5 mm (22%), and 85 implants (78%) had 4.0 mm. In length, 51 implants had 9 mm (46.8%), 25 had 11 mm (22.9%), and 33 implants were 13 mm (30.3%). There was no statistical difference between the abutment diameters (p > 0.05). Within the limitations of this study, it was possible to conclude that better behavior and lesser marginal bone loss were observed when using abutment heights greater than 2.5 mm of transmucosal portion and when placed implants with 13 mm length. Furthermore, this type of abutment showed a little incidence of failures within the period analyzed in our study.
Objectives: The present study compared two implants with different macrogeometries placed in healed alveolar sites, evaluating the insertion torque (ITV) and implant stability quotient (ISQ) values at three different periods. Methods: Seventy patients with a total of 100 dental implants were allocated into two groups (n = 50 per group): DuoCone implants (DC group) that included 28 implants in the maxilla and 22 in the mandible, and Maestro implants (MAE group) that included 26 in the maxilla and 24 in the mandible. The ITV was measured during the implant placement, and the ISQ values were measured immediately at implant placement (baseline) and after 30 and 45 days. Results: The mean and standard deviations of the ITV were statistically significant (p < 0.0001), 56.4 ± 6.41 Ncm for the DC group and 29.3 ± 9.65 Ncm for the MAE group. In the DC group, the ISQs ranged between 61.1 ± 3.78 and 69.8 ± 3.86, while the MAE group presented similar values compared with the other group, ranging between 61.9 ± 3.92 and 72.1 ± 2.37. Conclusions: The value of implant insertion torque did not influence the ISQ values measured immediately after implant placement. However, the ITV influenced the ISQ values measured in the two initial periods of osseointegration, with implants installed with lower torques presenting higher ISQ values.
This study investigated the effect of fracture strength and fracture mode characteristics related to reduced interocclusal space on computer-aided design/computer-aided manufacturing (CAD/CAM). ZrO 2 fixed partial denture (FPD) frameworks subjected to quasi-static loads. Materials and Methods: First, two dental implants (4 × 10 mm) were positioned simulating a three-unit FPD (second premolar and second molar abutments). The implants were distributed into two groups: control group (n = 10), positioned at the same level; and the test group (n = 10), where the interocclusal space corresponding to the second molar was reduced by 3 mm in relation to the second premolar to simulate a clinical situation. After FPD wax-up (25-mm long; connector height = 5 mm; connector width = 3 mm, proximal and lingual collar reinforcement), casting was made in a Co-Cr alloy to serve as a prototype. Upon scanning, screw-retained CAD/CAM ZrO 2 FPDs were fabricated for each group. Then, FPDs were subjected to quasi-static axial loading until fracture in the mid-occlusal pontic area using a universal testing machine at the crosshead speed of 0.5 mm/min. Next, the samples were analyzed by scanning electronic microscopy (SEM) to describe the fracture characteristics. Results: The mean fracture strength values for the control group (1,747.4 ± 122.3 N) and test group (1,817.7 ± 158.9 N) showed no significant difference (Student t test, P < .124). The SEM images of the fracture sites revealed two cleavage areas in the test group, providing representative sites with increased fracture energy storage in this group compared with the control group. Conclusion: Within the limitations of this study, the results showed that reduced interocclusal space and reduced length did not decrease the fracture strength of the ZrO 2 FPD frameworks.
Objective: The primary objective of the present retrospective clinical study was to evaluate and compare the clinical performance presented by castable abutments developed for the MT system versus intermediate machined abutments, specifically regarding prosthetic or implant fractures/loss; the secondary objective was to verify the looseness of the abutments and the behavior of the peri-implant soft tissues. Methods: This clinical retrospective study was conducted on patients rehabilitated between 2019 and 2020. Inclusion criteria were patients in good general health, with an implants-supporting single crown; with solid machined abutments (control group) or castable UCLA abutments; with a connection portion (base) machined in cobalt-chrome (test group) over Morse taper DuoCone implants in the posterior mandible area; and at least two years in function. Clinical assessment was carried out by the same professional, considering the following parameters: (A) prosthetic: (i) loosening of the fixation screw, (ii) fracture of the screw and (iii) the number of times the patient had some type of complication after the installation of the prostheses were evaluated; (B) biological: (i) without keratinized mucosa (KM), (ii) 1 mm or less, (iii) between 1 and 2 mm and (iv) greater than 2 mm of KM width; and the presence or absence of mucositis. Furthermore, radiographic evaluation was performed in order to assess the marginal bone loss. These evaluations permitted to compare the groups analyzed and patients enrolled. Data were statistically analyzed, with the level of significance set at α = 0.05. Results: 79 patients with 120 MT implants were evaluated (80 castable UCLA abutments and 40 machined solid abutments). The follow-up was from 2 to 4 years. There was a 100% implant survival rate. Therefore, the control group showed two fractured abutments (5%) and no abutment loosening (95% for prosthetic survival rate), whereas the test group showed no abutment fracture but nine loosening screws (11.3%) (100% for prosthetic survival rate). Keratinized mucosa was considered thin or absent in 19 implants in the control group (47.5%) and 42 in the test group (52.5%). Mucositis was found in 11 implants in the control group (27.5%) and 27 in the test group (33.8%). A positive correlation was observed between the width of keratinized mucosa and mucositis (r = 0.521, p = 0.002). The mean marginal bone loss was 2.3 mm, ranging from 1.1 to 5.8 mm. No correlation was observed when considering marginal bone loss versus the three parameters (implant diameter, implant length and time of the prosthesis in function). Conclusions: The results suggest that UCLA-type abutments are a viable option for rehabilitating implants with Morse taper connections, suggesting lower fracture risk. Further research is necessary to confirm these findings and thoroughly evaluate the clinical performance and long-term outcomes.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.