The purpose of this study was to evaluate the radiopacity of 5 root-end filling materials (white MTA-Angelus, grey MTA-Angelus, IRM, Super EBA and Sealer 26). Five specimens (10 mm diameter X 1 mm thickness) were made from each material and radiographed next to an aluminum stepwedge varying in thickness from 2 to 16 mm. Radiographs were digitized and the radiopacity of the materials was compared to that of the aluminum stepwedge using VIXWIN 2000 software in millimeters of aluminum (mm Al). Data were analyzed statistically by ANOVA and Tukey's test at 5% significance level. Radiopacity values varied from 3 mm Al to 5.9 mm Al. Sealer 26 and IRM presented the highest radiopacity values (p<0.05), while white/grey MTA and Super EBA presented the lowest radiopacity values (p<0.05). The tested root-end filling materials presented different radiopacities, white/grey MTA and Super EBA being the least radiopaque materials.

Considering that endodontic sealers release some components which may promote delay in the repair process, our purpose was to evaluate the tissue reaction promoted by MTA Plus and MTA Fillapex in comparison with AH Plus (standard control) and Endofill, which has a long clinical track record. One hundred rats were distributed into five groups: MTA Plus (Avalon Biom Inc., Bradenton, FL, USA), MTA Fillapex (Angelus, Londrina, PR, Brazil), AH Plus (Dentsply DeTrey GmbH, Konstanz, Germany), Endofill (Dentsply, Petrópolis, RJ, Brazil) and CG (control group, empty polyethylene tubes). The polyethylene tubes filled with sealers or empty (CG) were implanted into subcutaneous. After 7, 15, 30 and 60 days, the tubes surrounded by capsules were paraffin-embedded. In HE-stained sections, the volume density of inflammatory cells (VvIC) was estimated in the capsules. The number of interleukin-6-immunolabelled cells (IL-6), a pro-inflammatory cytokine, was also computed in the capsules. The birefringent collagen content was quantified in picrosirius-stained sections. Data were analysed by ANOVA and Tukey tests (p ≤ 0.05). At 7 days, the capsules showed moderate inflammatory reaction. In all groups, VvIC and IL-6-immunostained cells reduced significantly from 7 to 60 days. At 60 days, IL-6 immunoexpression was reduced significantly in MTA Plus and MTA Fillapex in comparison with AH Plus; no difference was found in the VvIC among MTA Plus, MTA Fillapex, AH Plus and CG whereas Endofill exhibited the highest VvIC. The reduction in VvIC was parallel to an increase in the collagen in all the groups, except Endofill. MTA Plus, MTA Fillapex and AH Plus induce a response that culminates in the regression of inflammation and formation of a fibrous capsule over time. The lower IL-6 immunoexpression in the capsules of MTA Plus and MTA Fillapex than AH Plus suggests that the immune response is suppressed more rapidly in the MTA-based sealers.

No abstract

The tissue reaction promoted by an experimental mineral trioxide aggregate sealer (MTAS) in the rat subcutaneous was evaluated by morphological and morphometric analyses. In the animals from each group (n = 20), polyethylene tubes filled with MTAS, Portland cement (PC) or MTA were implanted in the dorsal subcutaneous. In the control group, empty tubes were implanted. After 7, 14, 30, and 60 days, the specimens were fixed and embedded in paraffin. In the HE-stained sections, the numerical density of inflammatory cells (IC) in the capsule was evaluated and statistical analyses performed (p ≤ 0.05). The expression of osteopontin (OPN) was evaluated by immunohistochemistry. The von Kossa method for detection of calcified structures was also performed. A moderate inflammatory process in the capsule was seen in all groups, at 7 and 14 days. At 60 days, significant reduction in the number of IC was verified in comparison to initial periods; however, significant differences were not verified among the groups. OPN immunolabeling was observed in the fibroblasts cytoplasm of the capsule next to the implants. Structures von Kossa-positive were observed in the capsule adjacent to all materials implanted at 7, 14, and 30 days. The results strongly indicate that MTAS presents biocompatibility similarly to MTA and PC.