No abstract

Biomaterials and bone grafts, with the ability of stimulating tissue growth and bone consolidation, have been emerging as very promising strategies to treat bone fractures. Despite its well-known positive effects of biosilicate (BS) on osteogenesis, its use as bone grafts in critical situations such as bone defects of high dimensions or in non-consolidated fractures may not be sufficient to stimulate tissue repair. Consequently, several approaches have been explored to improve the bioactivity of BS. A promising strategy to reach this aim is the inclusion of an organic part, such as collagen, in order to mimic bone structure. Thus, the present study investigated the biological effects of marine spongin (SPG)-enriched BS composites on the process of healing, using a critical experimental model of cranial bone defect in rats. Histopathological and immunohistochemistry analyzes were performed after two and six weeks of implantation to investigate the effects of the material on bone repair (supplemental material-graphical abstract). Histological analysis demonstrated that for both BS and BS/SPG, similar findings were observed, with signs of material degradation, the presence of granulation tissue along the defect area and newly formed bone into the area of the defect. Additionally, histomorphometry showed that the control group presented higher values for Ob.S/BS (%) and for N.Ob/T.Ar (mm2) (six weeks post-surgery) compared to BS/SPG and higher values of N.Ob/T.Ar (mm2) compared to BS (two weeks post-surgery). Moreover, BS showed higher values for OV/TV (%) compared to BS/SPG (six weeks post-surgery). Also, VEGF immunohistochemistry was increased for BS (two weeks post-surgery) and for BS/SPG (six weeks) compared to CG. TGFb immunostaining was higher for BS compared to CG. The results of this study demonstrated that the BS and BS/SPG scaffolds were biocompatible and able to support bone formation in a critical bone defect in rats. Moreover, an increased VEGF immunostaining was observed in BS/SPG.

No abstract

This study evaluated the physicochemical and morphological properties of a marine sponge protein extract (PE) using scanning electron microscopy (SEM), Energy dispersive X-ray spectroscopy (EDS), analysis of mass loss and pH and in vitro and in vivo. Scanning electron microscopy showed that PE fibers present a granular aspect and irregular structure and the element carbon followed by oxygen was detected in the EDS analysis. Moreover, a 29% of mass loss was observed after 14 days and the pH slightly modified after 14 days. Cell viability of fibroblast cells (L929) of control and PE at a concentration of 25% demonstrated higher values compared to the groups. Osteoblast cell viability of PE at 25 and 50% was significantly higher. Comet assay on day 1 showed higher values for PE at 25%. In addition, in vivo experiments demonstrated that in the treated animals, the bone defects were filled with biomaterial particles, granulation tissue and some areas of newly formed bone. Furthermore, similar immunoexpression of Runx-2 and Cox-2 was observed. Taken together, all results suggest that PE is biocompatible, present non-citotoxicity in the in vitro studies (at the lower concentration) and in the in vivo studies and it can be considered as an alternative source of collagen for tissue engineering proposals.

No abstract

No abstract

The study comparing the bone regenerative capacity in an experimental model of cranial bone defects in rats, into 3 groups: G1: bone defects irradiated with photobiomodulation; G2: Biosilicate + photobiomodulation and G3: Biosilicate and Spongin + photobiomodulation. Histocompatibility and bone responses were performed after 15 and 45 days of implantation. Histological analysis demonstrated that photobiomodulation irradiated animals presented an increased amount of newly formed over time. Histomorphometry showed higher values for bone volume for G3 and G1, higher values for osteoid volume and number of osteoblasts observed for G3 compared to G2. TGF-β immunolabelling was higher for G2. The values found for VEGF were higher for biosilicate (with or without spongin) 15 days of implantation with an increased difference being observed for G1, 45 days after surgery. In conclusion, the stimulus provided by photobiomodulation associated to the biomimetic composite increased bone formation in the cranial bone defect in rats. Consequently, these data highlight the potential of the introduction of spongin into biosilicate and irradiated with photobiomodulation to improve the biological performance for bone regeneration applications.

This study characterized the morphological aspects of marine collagenspongin (SPG) extract from marine sponges, as well as, evaluating its in vitro and in vivo biological performance. Aplysina fulva marine sponge was used for the SPG extraction. It was investigated the physicochemical and morphological properties of SPG by using scanning electron microscopy, Fourier transform infrared spectroscopy, X-ray diffraction and compared to PMMA and bovine collagen. Additionally, the SPG cytotoxicity and its influence on cell proliferation, through in vitro tests. Moreover, the in vivo biological response was investigated using HIGHLIGHTS  Marine collagensponginextract from specimens of the sponge Aplysina fulva. Spongin has physicochemical and morphological properties analogous to human collagen.