Currently, polyurethane foam producers come across the several problems when petroleum-based polyols are replaced with low functionality biomass, or waste-based, polyols. In addition, the dilemma is intensified with regulations that require full or partial replacement of blowing agents that can cause high ozone depletion with alternatives like water, which causes the formation of CO2. Therefore, these gases diffuse out of the foam so quickly that the polymeric cell walls cannot withstand the pressure, consequently causing huge dimensional changes at ambient temperature and humidity. Even though the theoretical stoichiometric balance is correct, the reality shows that it is not enough. Therefore, polyethylene terephthalate waste-based polyol was chosen as a low functionality polyol which was modified with high functionality sucrose-based polyol in order to obtain dimensionally stable polyurethane foams in the density range of 30–40 kg/m3. These more stable foams are characterized by linear changes no higher than 0.5%, short-term water absorption by partial immersion no higher than 0.35 kg/m2, and water vapor resistance factors up to 50. In order to obtain thermally efficient polyurethane foams, conventional blowing agents and water systems were implemented, thus, assuring thermal conductivity values in the range of 0.0198–0.0204 W/(m·K) and obtaining products which conform to all the requirements for performance of sprayed and factory-made polyurethane foam standards EN 14315-1 and EN 13165.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.