We investigate the thermal conductivity of suspended graphene as a function of the density of defects, ND, introduced in a controllable way. High-quality graphene layers are synthesized using chemical vapor deposition, transferred onto a transmission electron microscopy grid, and suspended over ∼7.5 μm size square holes. Defects are induced by irradiation of graphene with the low-energy electron beam (20 keV) and quantified by the Raman D-to-G peak intensity ratio. As the defect density changes from 2.0 × 10(10) cm(-2) to 1.8 × 10(11) cm(-2) the thermal conductivity decreases from ∼(1.8 ± 0.2) × 10(3) W mK(-1) to ∼(4.0 ± 0.2) × 10(2) W mK(-1) near room temperature. At higher defect densities, the thermal conductivity reveals an intriguing saturation-type behavior at a relatively high value of ∼400 W mK(-1). The thermal conductivity dependence on the defect density is analyzed using the Boltzmann transport equation and molecular dynamics simulations. The results are important for understanding phonon - point defect scattering in two-dimensional systems and for practical applications of graphene in thermal management.
Organic-inorganic halide perovskites are intrinsically unstable when exposed to moisture and/or light. Additionally, the presence of lead in many perovskites raises toxicity concerns. Herein is reported a thin film of BaZrS3, a lead-free chalcogenide perovskite.Photoluminescence and X-ray diffraction measurements show that BaZrS3 is far more stable than methylammonium lead iodide (MAPbI3) in moist environments. Moisture-and lightinduced degradations in BaZrS3 and MAPbI3 are compared by using simulations and calculations based on density functional theory. The simulations reveal drastically slower degradation in BaZrS3 due to two factorsweak interaction with water, and very low rates of ion migration. BaZrS3 photo-detecting devices with photo-responsivity of ~46.5 mA W -1 are also reported. The devices retain ~60% of their initial photo-response after 4 weeks in ambient conditions. Similar MAPbI3 devices degrade rapidly and show ~95% decrease in photoresponsivity in just 4 days. The findings establish the superior stability of BaZrS3 and strengthen the case for its use in optoelectronics. New possibilities for thermoelectric energy conversion using these materials are also demonstrated.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.