A novel method for controllable fabrication of a superhydrophobic surface with a water contact angle of 162 ± 1° and a sliding angle of 3 ± 0.5° on copper substrate is reported in this Research Article. The facile and low-cost fabrication process is composed from the electrodeposition in traditional Watts bath and the heat-treatment in the presence of (heptadecafluoro-1,1,2,2-tetradecyl) triethoxysilane (AC-FAS). The superhydrophobicity of the fabricated surface results from its pine-cone-like hierarchical micro-nanostructure and the assembly of low-surface-energy fluorinated components on it. The superhydrophobic surface exhibits high microhardness and excellent mechanical abrasion resistance because it maintains superhydrophobicity after mechanical abrasion against 800 grit SiC sandpaper for 1.0 m at the applied pressure of 4.80 kPa. Moreover, the superhydrophobic surface has good chemical stability in both acidic and alkaline environments. The potentiodynamic polarization and electrochemical impedance spectroscopy test shows that the as-prepared superhydrophobic surface has excellent corrosion resistance that can provide effective protection for the bare Cu substrate. In addition, the as-prepared superhydrophobic surface has self-cleaning ability. It is believed that the facile and low-cost method offer an effective strategy and promising industrial applications for fabricating superhydrophobic surfaces on various metallic materials.
Yarn supercapacitors are promising power sources for flexible electronic applications that require conventional fabric-like durability and wearer comfort. Carbon nanotube (CNT) yarn is an attractive choice for constructing yarn supercapacitors used in wearable textiles because of its high strength and flexibility. However, low capacitance and energy density limits the use of pure CNT yarn in wearable high-energy density devices. Here, transitional metal oxide pseudocapacitive materials NiO and Co3 O4 are deposited on as-spun CNT yarn surface using a simple electrodeposition process. The Co3 O4 deposited on the CNT yarn surface forms a uniform hybridized CNT@Co3 O4 layer. The two-ply supercapacitors formed from the CNT@Co3 O4 composite yarns display excellent electrochemical properties with very high capacitance of 52.6 mF cm(-2) and energy density of 1.10 μWh cm(-2) . The high performance two-ply CNT@Co3 O4 yarn supercapacitors are mechanically and electrochemically robust to meet the high performance requirements of power sources for wearable electronics.
Au nanoparticles are successfully decorated onto graphene oxide (GO) sheets with the aid of supercritical carbon dioxide (ScCO) fluid. The synthesized nanocomposite (Sc-Au/GO) was characterized by X-ray diffraction (XRD), Raman spectroscopy, thermal gravimetric analysis (TGA), and transmission electron microscopy (TEM). The characterization results show that the Au nanoparticles are featured with face-centered cubic crystal structure and disperse well on the GO nanosheet surfaces with average diameters of 4-10 nm. The tribological behaviors of Sc-Au/GO as lubricating additive in PAO6 oil were investigated using a ball-on-disc friction tester, and a control experiment by respectively adding GO, nano-Au particles, and Au/GO produced in the absence of ScCO was performed as well. It is found that Sc-Au/GO exhibits the best lubricating performances among all the samples tested. When 0.10 wt % Sc-Au/GO is dispersed into PAO6 oil, the friction coefficient and wear rate are respectively reduced by 33.6% and 72.8% as compared to that of the pure PAO6 oil, indicating that Sc-Au/GO is an energy efficient lubricant additive. A possible lubricating mechanism of Sc-Au/GO additive in PAO6 oil has been tentatively proposed on the basis of the analyzed results of the worn surface examined by scanning electron microscopy (SEM), Raman spectroscopy, and X-ray photoelectron spectroscopy (XPS).
Graphene oxide dotted with nickel nanoparticles (Sc-Ni/GO) was synthesized by chemical deposition with the assistance of supercritical carbon dioxide (scCO2). The deposited Ni nanoparticles with diameters less than 5 nm are uniformly anchored on the surfaces of GO nanosheets. The as-prepared Sc-Ni/GO composites were employed as lubricating additives in paraffin oil and their tribological properties were tested using a four-ball tribometer. The results demonstrate that the Sc-Ni/GO composites are efficient lubricant additives. Adding 0.08 wt % Sc-Ni/GO into paraffin oil can reduce the friction coefficient and wear scar diameter by 32 and 42%, respectively, in comparison with the pure oil. In addition, Sc-Ni/GO composites exhibit superior lubricating performances than nano-Ni, GO nanosheets, and Ni/GO composites produced without the aid of scCO2. Such excellent lubricating properties of the Sc-Ni/GO composites derive from the synergistic lubricating actions of Ni nanoparticles and GO nanosheets during the rubbing process. The synergistic lubricating actions are closely related to the microstructure of the nanocomposites and the characteristic features of transfer film formed on the contact steel balls. The anchored Ni nanoparticles with smaller size and more uniform distribution on GO surfaces and the thin transfer film formed on the contact balls favor the full play of the synergistic actions.
Strong and flexible two-ply carbon nanotube yarn supercapacitors are electrical double layer capacitors that possess relatively low energy storage capacity. Pseudocapacitance metal oxides such as MnO₂ are well known for their high electrochemical performance and can be coated on carbon nanotube yarns to significantly improve the performance of two-ply carbon nanotube yarn supercapacitors. We produced a high performance asymmetric two-ply yarn supercapacitor from as-spun CNT yarn and CNT@Mn₂2 composite yarn in aqueous electrolyte. The as-spun CNT yarn serves as negative electrode and the CNT@MnO₂ composite yarn as positive electrode. This asymmetric architecture allows the operating potential window to be extended from 1.0 to 2.0 V and results in much higher energy and power densities than the reference symmetric two-ply yarn supercapacitors, reaching 42.0 Wh kg(-1) at a lower power density of 483.7 W kg(-1), and 28.02 Wh kg(-1) at a higher power density of 19,250 W kg(-1). The asymmetric supercapacitor can sustain cyclic charge-discharge and repeated folding/unfolding actions without suffering significant deterioration of specific capacitance. The combination of high strength, flexibility and electrochemical performance makes the asymmetric two-ply yarn supercapacitor a suitable power source for flexible electronic devices for applications that require high durability and wearer comfort.
Silver nanoparticle-decorated graphene nanocomposites were synthesized by a facile chemical reduction approach with the assistance of supercritical CO2 (ScCO2). The silver nanoparticles with diameters of 2–16 nm are uniformly distributed and firmly anchored on graphene nanosheets. The tribological properties of the as-synthesized nanocomposites as lubricant additives in engine oil were investigated by a four-ball tribometer. The engine oil with 0.06~0.10 wt.% Sc-Ag/GN nanocomposites displays remarkable lubricating performance, superior than the pure engine oil, the engine oil containing zinc dialkyl dithiophosphate (ZDDP), as well as the oil dispersed with the single nanomaterial of graphene oxides (GOs) and nano-Ag particles alone. The remarkable lubricating behaviors of Sc-Ag/GN probably derive from the synergistic interactions of nano-Ag and graphene in the nanocomposite and the action of the formed protective film on the contact balls. The anchored nano-Ag particles on graphene expand the interlamination spaces of graphene nanosheets and can prevent them from restacking during the rubbing process, resulting in the full play of lubricating activity of graphene. The formed protective film on the friction pairs significantly reduces the surface roughness of the sliding balls and hence preventing them from direct interaction during the sliding process.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.