Thin films of the high-temperature superconductor YBa 2 Cu 3 O 7 ؊ ␦ exhibit both a large critical current (the superconducting current density generally lies between 10 11 and 10 12 A m −2 at 4.2 K in zero magnetic field) and a decrease in such currents with magnetic field that point to the importance of strong vortex pinning along extended defects 1,2 . But it has hitherto been unclear which types of defect-dislocations, grain boundaries, surface corrugations and anti-phase boundaries-are responsible. Here we make use of a sequential etching technique to address this question. We find that both edge and screw dislocations, which can be mapped

No abstract

No abstract

At low temperatures dislocations are the dominant flux-pinning centers in thin films of YBa 2 Cu 3 O 7Ϫ␦ deposited on ͑100͒ SrTiO 3 substrates ͓B. Dam et al., Nature ͑London͒ 399, 439 ͑1999͔͒. Using a wet-chemical etching technique in combination with atomic force microscopy, both the length and the lateral dislocation distribution are determined in laser ablated YBa 2 Cu 3 O 7Ϫ␦ films. We find that ͑i͒ dislocations are induced in the first stages of film growth, i.e., close to the substrate-film interface, and persist all the way up to the film surface parallel to the c axis, resulting in a uniform length distribution, and ͑ii͒ the radial dislocation distribution function exhibits a universal behavior: it approaches zero at small distances, indicating short-range ordering of the defects. This self-organization of the growth-induced correlated disorder makes epitaxial films completely different from single crystals with randomly distributed columnar defects created by means of heavy-ion irradiation. Since the substrate temperature can be used to tune the dislocation density n disl over almost two orders of magnitude ͑ϳ1-100/m 2 ͒, the mechanism by which dislocations are induced is closely related to the YBa 2 Cu 3 O 7Ϫ␦ nucleation and growth mechanism. We present evidence for preferential precipitation in the first monolayer and precipitate generated dislocations.

No abstract