Mineral trioxide aggregate (MTA) and Portland cement (PC) are calcium silicate cements. They have similar physicochemical, mechanical and biological properties. The addition of zirconium oxide (ZrO2) to PC provides radiopacity. Silver nanoparticles (AgNPs) may improve some properties of cements. The aim of this study was to evaluate the effect of AgNPs on physicochemical/mechanical properties and antibacterial activity of white MTA (WMTA) and PC associated with ZrO2. The following materials were evaluated: WMTA; PC 70% + ZrO2 30%; WMTA+ AgNPs; and PC 70% + ZrO2 30% + AgNPs. The study evaluated radiopacity, setting time, pH, compressive strength and solubility. For radiopacity analysis, radiographs were made alongside an aluminum (Al) step wedge. To evaluate the antibacterial activity, direct contact test was performed on planktonic cells and Enterococcus faecalis biofilm induced on bovine root dentin for 14 days. The experimental periods were 5 and 15 h. Data were obtained as CFU mL-1. The obtained data were submitted to ANOVA and Tukey tests (p<0.05). The addition of AgNPs to WMTA increased the pH, lowered the solubility and the initial and final setting times. The addition of AgNPs to PC/ZrO2 maintained the pH, lowered the solubility, and increased the setting time and compressive strength. The radiopacity of all materials was higher than 4 mmAl. The addition of AgNPs promoted an increase in antibacterial activity for calcium silicate cements and favored the physicochemical and mechanical properties of the materials.
The aim of the current study was to evaluate the presence of debris and smear layer after endodontic irrigation with different formulations of 2% chlorhexidine gluconate (CHX) and its effects on the push-out bond strength of an epoxy-based sealer on the radicular dentin. One hundred extracted human canines were prepared to F5 instrument and irrigated with 2.5% sodium hypochlorite and 17% ethylenediaminetetraacetic acid. Fifty teeth were divided into five groups (n = 10), according to the final irrigation protocol with different 2% CHX formulations: G1 (control, no final rinse irrigation), G2 (CHX solution), G3 (CHX gel), G4 (Concepsis), and G5 (CHX Plus). In sequence, the specimens were submitted to scanning electron microscopy (SEM) analysis, in the cervical-medium and medium-apical segments, to evaluate the presence of debris and smear layer. The other 50 teeth were treated equally to a SEM study, but with the root canals filled with an epoxy-based endodontic sealer and submitted to a push-out bond strength test, in the cervical, middle, and apical thirds. G2, G3, G4, and G5 provided higher precipitation of the debris and smear layer than G1 (P < 0.05), but these groups were similar to each other (P > 0.05), in both segments. The values obtained in the push out test did not differ between groups, independent of the radicular third (P > 0.05). The CHXs formulations caused precipitation of the debris and smear layer on the radicular dentin, but these residues did not interfere in the push-out bond strength of the epoxy-based sealer.
Objective Mineral Trioxide Aggregate (MTA) is a calcium silicate cement composed of Portland cement (PC) and bismuth oxide. Hydroxyapatite has been incorporated to enhance mechanical and biological properties of dental materials. This study evaluated physicochemical and mechanical properties and antibiofilm activity of MTA and PC associated with zirconium oxide (ZrO2) and hydroxyapatite nanoparticles (HAn).Material and Methods White MTA (Angelus, Brazil); PC (70%)+ZrO2 (30%); PC (60%)+ZrO2 (30%)+HAn (10%); PC (50%)+ZrO2 (30%)+HAn (20%) were evaluated. The pH was assessed by a digital pH-meter and solubility by mass loss. Setting time was evaluated by using Gilmore needles. Compressive strength was analyzed by mechanical test. Samples were radiographed alongside an aluminum step wedge to evaluate radiopacity. For the antibiofilm evaluation, materials were placed in direct contact with E. faecalis biofilm induced on dentine blocks. The number of colony-forming units (CFU mL-1) in the remaining biolfilm was evaluated. The results were submitted to ANOVA and the Tukey test, with 5% significance.Results There was no difference in pH levels of PC+ZrO2, PC+ZrO2+HAn (10%) and PC+ZrO2+HAn (20%) (p>0.05) and these cements presented higher pH levels than MTA (p<0.05). The highest solubility was observed in PC+ZrO2+HAn (10%) and PC+ZrO2+HAn (20%) (p<0.05). MTA had the shortest initial setting time (p<0.05). All the materials showed radiopacity higher than 3 mmAl. PC+ZrO2 and MTA had the highest compressive strength (p<0.05). Materials did not completely neutralize the bacterial biofilm, but the association with HAn provided greater bacterial reduction than MTA and PC+ZrO2 (p<0.05) after the post-manipulation period of 2 days.Conclusions The addition of HAn to PC associated with ZrO2 harmed the compressive strength and solubility. On the other hand, HAn did not change the pH and the initial setting time, but improved the radiopacity (HAn 10%), the final setting time and the E. faecalis antibiofilm activity of the cement.
Objective: To quantify the persistence of residues after endo dontic retreatment related to the root canal obturation technique (lateral compaction or single cone) previously performed and the solvent used (xylol or EndosolvR) in the cervical and root apical segment using digital radiograph. Materials and methods:Forty root canals were prepared using the F2 instrument and filled with gutta-percha and AH Plus, 20 canals using #25 point by lateral compaction and the other 20 using F2 point by single cone. The root canals were transversely sectioned, and two segments (cervical and apical) were obtained. Radiographs were taken from the segment in buccolingual and mesiodistal direction, as well as the area that was originally filled with the root canal obturation was measured using ImageJ. After the specimens were set on special devices, the obturations were removed using the rotary system and divided into four groups (n = 10): G1 -lateral compaction and xylol; G2 -lateral compaction and EndosolvR; G3 -single cone and xylol; and G4 -single cone and Endosolv-R. A new radiograph was taken and the area occupied by residues was measured. The persistence of residues was obtained from the obturation remaining in the root canal in percentage. The data were analyzed using Kruskal-Wallis test (p = 0.05).Results: There was no difference among the examined groups, regardless of the radicular segment or the radiograph direction (p > 0.05). Conclusion:The endodontic retreatment using xylol or EndosolvR in the obturations previously performed by lateral compaction or single cone technique presented similar persis tence of residues in the root canal, regardless of the radicular segment.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.