Industrial processes such as the extraction and processing of building and dimension stone and the manufacturing of ferroalloys generate large amounts of waste, which can cause environmental damage. Therefore, the development of new techniques for recycling and reusing industrial waste would be useful for minimizing the environmental impacts of these activities. This paper presents the incorporation of soapstone powder and FeeSieMn slag in clayelime brick as a partial substitution for agglomerate (lime) because these residues meet the standard specification for the chemical composition of a pozzolanic material. The results show that brick samples where 25% lime is substituted by waste residues achieved a compressive strength above 2.0 MPa, which is within the standard specification, after 28 days of curing (soapstone powder) or 60 days of curing (soapstone powder and FeeSieMn slag). These materials were classified as class II, non-inert residues.

No abstract

No abstract

Esse artigo apresenta estudos de concentração de finos de minério de manganês (estocados como rejeito) da Mineração Morro da Mina/RDM em mesa oscilatória, visando à obtenção de concentrados para serem empregados na indústria metalúrgica. Os teores de Mn, na amostra global e nas frações acima e abaixo de 0,074 mm, eram de 28,30; 26,84 e 31,31%, respectivamente. Pela análise granulométrica, verificou-se que 80% desses finos encontravam-se abaixo de 0,149 mm. Nas condições otimizadas dos ensaios de concentração (15% de sólidos na polpa e ângulo de inclinação da mesa igual a 3º), foram obtidas recuperações de manganês da amostra global, acima e abaixo de 0,074 mm de 77, 81 e 62%, respectivamente. Os teores de manganês e impurezas, nos concentrados, para as amostras estudadas, satisfizeram as especificações químicas dos produtos comercializados pela empresa.
This article presents the results of fine manganese ore from Morro da Mina Mine/RDM concentration studies using oscillatory table in order to obtain concentrates to be used in metallurgical industries. The global, the fractions above and below 0,074 mm samples manganese contents were 28,30; 26,84 and 31,31%, respectively. It was observed that 80% of the particles in global sample were below 0,149 mm. For the optimized table concentration test, solids pulp with 15% and table inclination angle of 3º, the manganese recoveries of the global, fraction above 0,074 and below 0,074 mm samples were of 77, 81 and 62%, respectively. The manganese and impurities contents in those concentrates satisfied the chemical specifications of Morro da Mina Mine/RDM products

No abstract

RESUMOOs minérios de manganês provenientes da mina do Azul são importante matéria-prima na produção de ferro-ligas de manganês. Visando melhorias no beneficiamento e no processo de fabricação destas ligas, foi realizada a caracterização do produto Granulado da unidade do Azul-VALE/Manganês. Foi obtida uma amostra representativa desta mina e realizada análise granulométrica, onde se verificou a ocorrência de 80% das partículas abaixo de 22,6mm e 50% abaixo de 12,5mm. Considerou-se como granulado a fração menor que 37,5mm e maior que 6,3mm, que é a mais abundante neste minério e comumente destinada às usinas de ferro-ligas. A fração entre 37,5mm e 6,3mm foi amostrada e foram realizadas análises termogravimétrica, química dos elementos majoritários e identificadas as fases minerais presentes. A análise térmica (TG-DTA) identificou perda de massa em torno de 300 o C, 500 o C, 700 o C, 900 o C e 1000 o C associadas à decomposição térmica de algumas fases minerais presentes. Chemical, physical and mineralogical characterization of Azul Mine manganese lump product ABSTRACTThe manganese ores from Azul mine are important raw materials for ferro alloys production. For improvements in the manganese ferro alloys production, Azul's lump ore product was characterized. A representative sample from the mine has been obtained and their particle sizes were classified. The size distribution showed that 80% of particles were below 22.6mm and 50% were below 12.5mm. The particles with sizes between 37.5mm and 6.3mm were named lump ore product. The fraction between 37.5mm and 6.3mm was submitted to chemical and mineralogical characterization. The TGA tests showed weight losses in 300 o C, 500 o C, 700 o C, 900 o C and 1000 o C due, mainly, the high manganese oxides decompositions. 3 ] appear as minor constituents (Pyrolusite, magnetite e gibbsite were identified by optical microscopy).

No abstract

ResumoVisando a melhorias no benefi ciamento e no processo de fabricação de ferroligas de manganês, foi realizada a caracterização de uma tipologia predominante de minério de manganês, de ocorrência na região de Carajás, PA, BR. Obteve-se uma amostra representativa da tipologia e foram realizadas análise granulométrica por peneiramento e análise química, por ICP-AES. Foram identifi cadas por difratometria de raios X as fases minerais majoritárias. Um estudo termogravimétrico foi desenvolvido para verifi car a estabilidade térmica, ao ar, das fases minerais majoritárias. Observou-se que 19,3% da amostra encontram-se abaixo de 6,3mm. O teor de manganês no minério foi de 52,63% em peso, com 1,92% de sílica, 0,17% de fósforo e 3,13% de ferro. Foram identifi cados, na amostra, os óxidos de manganês criptomelana, todorokita e pirolusita, com goethita, quartzo, gibbisita e caolinita compondo a ganga. Para a amostra estudada, observou-se a decomposição térmica dos óxidos criptomelana e pirolusita, em torno de 600 o C, ao ar. Em torno de 950 o C, teve início a transformação de Mn 2 O 3 em Mn 3 O 4.Palavras-chave: Minério de manganês, caracterização tipológica, decomposição térmica. Abstract In order to improve manganese-iron alloy production processes, an important Brazilian manganese ore typology, placed in Carajás, PA, was characterized. A representative sample was obtained from mine. The particle size determination was performed by screening, followed by chemical analysis using plasma spectrometry (ICP-AES). The physical properties studied included density, surface area and porosity measurements (BET). The mineral constituents was identifi ed and quantifi ed by X-ray diffraction. A termogravimetrical study was done in order to