No abstract

Macrophage activation can be modulated by biomaterial topography according to the biological scale (micrometric and nanometric range). In this study, we investigated the effect of fiber diameter and fiber alignment of electrospun poly(L-lactic) (PLLA) scaffolds on macrophage RAW 264.7 activation and secretion of proinflammatory cytokines and chemokines at 24 h and 7 days. Macrophages were cultured on four different types of fibrous PLLA scaffold (aligned microfibers, aligned nanofibers, random microfibers, and random nanofibers) and on PLLA film (used as a reference). Substrate topography was found to influence the immune response activated by macrophages, especially in the early inflammation stage. Secretion of proinflammatory molecules by macrophage cells was chiefly dependent on fiber diameter. In particular, nanofibrous PLLA scaffolds minimized the inflammatory response when compared with films and microfibrous scaffolds. The histological evaluation demonstrated a higher number of foreign body giant cells on the PLLA film than on the micro- and nanofibrous scaffolds. In summary, our results indicate that the diameter of electrospun PLLA fibers, rather than fiber alignment, plays a relevant role in influencing in vitro macrophage activation and secretion of proinflammatory molecules.

In this study, we investigated whether multipotent (human-bone-marrow-derived mesenchymal stem cells [hBM-MSCs]) and pluripotent stem cells (murine-induced pluripotent stem cells [iPSCs] and murine embryonic stem cells [ESCs]) respond to nanocomposite fibrous mats of poly(L-lactic acid) (PLLA) loaded with 1 or 8 wt % of calcium-deficient nanohydroxyapatite (d-HAp). Remarkably, the dispersion of different amounts of d-HAp to PLLA produced a set of materials (PLLA/d-HAp) with similar architectures and tunable mechanical properties. After 3 weeks of culture in the absence of soluble osteogenic factors, we observed the expression of osteogenic markers, including the deposition of bone matrix proteins, in multi/pluripotent cells only grown on PLLA/d-HAp nanocomposites, whereas the osteogenic differentiation was absent on stem-cell-neat PLLA cultures. Interestingly, this phenomenon was confined only in hBM-MSCs, murine iPSCs, and ESCs grown on direct contact with the PLLA/d-HAp mats. Altogether, these results indicate that the osteogenic differentiation effect of these electrospun PLLA/d-HAp nanocomposites was independent of the stem cell type and highlight the direct interaction of stem cell-polymeric nanocomposite and the mechanical properties acquired by the PLLA/d-HAp nanocomposites as key steps for the differentiation process.

No abstract

Bioactive glasses synthesized by the sol-gel technique possess many of the qualities associated with an ideal scaffold material for a bone graft substitute. In view of the potential clinical applications, we performed a detailed in vitro study of the biological reactivity of synthesized 58S bioactive glass containing-zinc, in terms of osteoblast morphology, proliferation, and deposition of a mineralized extracellular matrix (ECM). Human Sarcoma Osteoblast (SAOS-2) cells were used to i) assess cytotoxicity by lactate dehydrogenase (LDH) release and ii) evaluate the deposition of a calcified extracellular matrix by ELISA assay and quantitative RT-PCR (qRT-PCR). In comparison with pure silica and 58S, the 58S-Zn0.4 bioglass showed a significant increase in cellular proliferation and deposition of ECM components such as decorin, fibronectin, osteocalcin, osteonectin, osteopontin, type-I and -III collagens. Calcium deposition was significantly higher than on pure silica and 58S samples. Also Alkaline phosphatase (ALP) activity and its protein content was higher with respect to pure silica and 58S. qRT-PCR analysis revealed the up-regulation of type-I collagen, bone sialoprotein and osteopontin genes. All together these results demonstrate the cytocompatibility of 58S-Zn0.4 bioglass and its capability to promote osteoblast differentiation.

In bone tissue engineering, bioglass coating of titanium (Ti) scaffolds has drawn attention as a method to improve osteointegration and implant fixation. In this in vitro study, bioactive glass layers with an approximate thickness of 1 microm were deposited at 200 degrees C onto a three-dimensional Ti-6Al-4V scaffold using a radio frequency (r.f.) magnetron sputtering system. After incubation with SAOS-2 human osteoblasts, in comparison with the uncoated scaffolds, the bioglass-coated scaffolds showed a twofold increase in cell proliferation (p < 0.05) up to 68.4 x 10(6), and enhanced the deposition of extracellular matrix components such as decorin, fibronectin, osteocalcin, osteonectin, osteopontin, and type-I and -III collagens (p < 0.05). Calcium deposition was twofold greater on the bioglass-coated scaffolds (p < 0.05). The immunofluorescence related to the preceding bone matrix proteins and calcium showed their colocalization to the cell-rich areas. Alkaline phosphatase activity increased twofold (p < 0.001) and its protein content was threefold higher with respect to the uncoated sample. Quantitative reverse transcriptase-polymerase chain reaction analysis revealed upregulated transcription specific for type-I collagen and osteopontin (p < 0.001). All together, these results demonstrate that the bioglass coating of the three-dimensional Ti scaffolds by the r.f. magnetron sputtering technique determines an in vitro increase of the bone matrix elaboration and may potentially have a clinical benefit.

The use of stem cells in regenerative medicine is an appealing area of research that has received a great deal of interest in recent years. The population called human adipose tissue-derived stem cells (hASCs) share many of the characteristic of its counterpart of marrow including extensive proliferative potential and the ability to undergo multilineage differentiation along classical mesenchymal lineages: adipogenesis, chondrogenesis, osteogenesis, and myogenesis. The aim of this study was to evaluate with biochemical and morphological methods the adhesion and differentiation of hASCs grown on trabecular titanium scaffolds. The hASCs isolated from subcutaneous adipose tissue after digestion with collagenase were seeded on monolayer and on trabecular titanium scaffolds and incubated at 37 degrees C in 5% CO(2) with osteogenic medium or control medium.The results showed that hASCs were able to adhere to titanium scaffolds, to proliferate, to acquire an osteoblastic-like phenotype, and to produce a calcified extracellular matrix with protein, such as, decorin, fibronectin, osteocalcin, osteonectin, osteopontin, and type I collagen. These data suggest that this kind of scaffold/cells construct is effective to regenerate damaged tissue and to restore the function of bone tissue.

Adherence of oral bacteria to the surface of dental restorative materials is considered an important step in the development of secondary caries and periodontal disease. The aim of this study was to investigate and compare the adherence of different restorative materials to Streptococcus mutans strain (CCUG35176) in order to ascertain possible differences. The materials tested ranged across different classes including: flowable composites (Gradia Direct LoFlo; Filtek Supreme XT Flowable), anterior composites (Gradia Direct Anterior), universal composites (Filtek Supreme XT), packable composites (Filtek Silorane; Filtek P60), glass-ionomers (Fuji IX Gp Extra; Equia) and a control reference material (Thermanox plastic coverlips). Bacterial suspension was deposited onto each material and the adhesion was evaluated trough the colony forming units (CFUs) determination. Packable silorane-based composite was found to be less adhesive than posterior packable composite P60, flowable composites and glass ionomers. The fluoride of glass ionomers did not prevent the attachment of S. mutans; furthermore, after roughness analysis and SEM investigations, the hypothesis that the difference in bacterial adhesion can be determined by the particular surface chemistry of the material itself as well as by different electrostatic forces between bacteria and restorative surfaces must be given serious consideration.