A phase change material (PCM) from a mixture of plant oils was incorporated into electrospun poly(vinyl alcohol) (PVA) nanofibers using an emulsion electrospinning technique. Effects of PCM and PVA content in the emulsions on nanofiber morphology, heat properties, and phase change stability were examined. Higher PCM loadings in the nanofibers led to increased fiber diameter, gouged fiber surfaces, and higher heat enthalpies. The fibers maintained their morphological integrity even if the PCM melted. They showed reliable heat-regulating performance which can undergo at least 100 cycles of phase change. Such PCM fibers may be used for the development of thermoregulating fabrics or in passive heat storage devices.
In the present study, core-reinforced braided composite rods (BCRs) were developed and characterized for strain sensing capability. A mixture of carbon and glass fibre was used in the core, which was surrounded by a braided cover of polyester fibres. Three compositions of core with different carbon fibre/glass fibre weight ratios (23/77, 47/53, and 100/0) were studied to find out the optimum composition for both strain sensitivity and mechanical performance. The influence of carbon fibre positioning in BCR cross-section on the strain sensing behaviour was also investigated. Strain sensing property of BCRs was characterized by measuring the change in electrical resistance with flexural strain. It was observed that BCRs exhibited increase (positive response) or decrease (negative response) in electrical resistance depending on carbon fibre positioning. The BCR with lowest amount of carbon fibre was found to give the best strain sensitivity as well as the highest tensile strength and breaking extension. The developed BCRs showed reversible strain sensing behaviour under cyclic flexural loading with a maximum gauge factor of 23.4 at very low strain level (0.55%). Concrete beams reinforced with the optimum BCR (23/77) also exhibited strain sensing under cyclic flexural strain, although the piezoresistive behaviour in this case was irreversible.
The effect of UV irradiation and micro‐ and nano‐TiO2 as well as titanate nanotubes (TiNT) on the phase morphology and thermal properties of the electrospun PCL composite fibers was investigated. Polycaprolactone (PCL)/TiO2 (micro‐ and nano‐TiO2 as well as titanate nanotubes) composite fibers were prepared by electrospinning a polymer solution. The PCL and PCL/TiO2 composite fibers were exposed to UV light at irradiation times of 5 and 10 days. After UV irradiation the crystallinity of the electrospun PCL/TiNTcomposite fibers increased because of the large specific surface area of TiNT. The thermal stability of the PCL/TiNT electrospun composite fibers increased due to the formation of crosslinking structure after UV irradiation. The SEM analysis suggests that after UV radiation the fibers showed high degree of degradation due to the high number of fibers breakages and fibers surface voids. The results of FTIR spectroscopy confirmed that the TiO2 particles enhance the degradation process because of their photocatalytic activity. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016, 133, 43539.
No abstract
Cells grown on bioactive matrices have immensely advanced many aspects of biomedical research related to drug delivery and tissue engineering. Our main objective was to perform simple evaluation of the structural and biotic qualities of cell scaffolds made of affordable biomaterials for liver cell line (HepG2) cultivation in vitro. In this work the electrospun matrix made of synthetic polyester poly(ε-caprolactone) (PCL) was compared with the natural protein-based extracellular matrix isolated from porcine liver (ECM). Mechanical and structural analysis showed that ECM was about 12 times less resistant to tensile stress while it had significantly larger pore size and twice smaller water contact angle than PCL. Bioactivity assessment included comparison of cell growth and transfection efficiency on cell-seeded scaffolds. Despite the differences in composition and structure between the two respective matrices, the rate of cell spreading and the percentage of transfected cells on both scaffolds were fairly comparable. These results suggest that in an attempt to produce simple, cell carrying structures that adequately simulate the natural scaffold, one can rely on PCL electrospun mats.
Limbal Stem Cell Deficiency (LSCD) is a very serious and painful disease that often results in impaired vision. Cultivation of limbal stem cells for clinical application is usually performed on carriers such as amniotic membrane or surgical fibrin gel. Transplantation of these grafts is associated with the risk of local postoperative infection that can destroy the graft and devoid therapeutic benefit. For this reason, electrospun scaffolds are good alternatives, as proven to mimic the natural cells surroundings, while their fabrication technique is versatile with regard to polymer functionalization and scaffolds architecture. This study considers the development of poly(ε-caprolactone) (PCL) immune-compatible and biodegradable electrospun scaffolds, comprising cefuroxime (CF) or titanium dioxide (TiO2) active components, that provide both bactericidal activity against eye infections and support of limbal stem cells growth in vitro. The PCL/CF scaffolds were prepared by blend electrospinning, while functionalization with the TiO2 particles was performed by ultrasonic post-processing treatment. The fabricated scaffolds were evaluated in regard to their physical structure, wetting ability, static and dynamic mechanical behaviour, antimicrobial efficiency and drug release, through scanning electron microscopy, water contact angle measurement, tensile testing and dynamic mechanical analysis, antimicrobial tests and UV-Vis spectroscopy, respectively. Human limbal stem cells, isolated from surgical remains of human cadaveric cornea, were cultured on the PCL/CF and PCL/TiO2 scaffolds and further identified through immunocytochemistry in terms of cell type thus were stained against p63 marker for limbal stem cells, a nuclear transcription factor and cytokeratin 3 (CK3), a corneal epithelial differentiation marker. The electrospun PCL/CF and PCL/TiO2 successfully supported the adhesion, proliferation and differentiation of the cultivated limbal cells and provided the antimicrobial effect against Pseudomonas aeruginosa, Staphylococcus aureus and Candida albicans.
One of the largest fields of application of electrospun materials is the biomedical field, including development of scaffolds for tissue engineering, drug delivery and wound healing. Electrospinning appears as a promising technique in terms of scaffolds composition and architecture, which is the main aspect of this review paper, with a special attention to natural polymers including collagen, fibrinogen, silk fibroin, chitosan, chitin etc. Thanks to the adaptability of the electrospinning process, versatile hybrid, custom tailored structure scaffolds have been reported. The same is achieved due to the vast biomaterials’ processability as well as modifications of the basic electrospinning set-up and its combination with other techniques, simultaneously or by post-processing.
AimTo investigate the impact of synthetic electrospun polyurethane (PU) and polycaprolactone (PCL) nanoscaffolds, before and after hydrolytic surface modification, on viability and differentiation of cultured human eye epithelial cells, in comparison with natural scaffolds: fibrin and human amniotic membrane.MethodsHuman placenta was taken at elective cesarean delivery. Fibrin scaffolds were prepared from commercial fibrin glue kits. Nanoscaffolds were fabricated by electrospinning. Limbal cells were isolated from surpluses of human cadaveric cornea and seeded on feeder 3T3 cells. The scaffolds used for viability testing and immunofluorescence analysis were amniotic membrane, fibrin, PU, and PCL nanoscaffolds, with or without prior NaOH treatment.ResultsScanning electron microscope photographs of all tested scaffolds showed good colony spreading of seeded limbal cells. There was a significant difference in viability performance between cells with highest viability cultured on tissue culture plastic and cells cultured on all other scaffolds. On the other hand, electrospun PU, PCL, and electrospun PCL treated with NaOH had more than 80% of limbal cells positive for stem cell marker p63 compared to only 27%of p63 positive cells on fibrin.ConclusionNatural scaffolds, fibrin and amniotic membrane, showed better cell viability than electrospun scaffolds. On the contrary, high percentages of p63 positive cells obtained on these scaffolds still makes them good candidates for efficient delivery systems for therapeutic purposes.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.