SUMMARY
Objective:
The objective of this study was to evaluate the in vivo effectiveness of air spray to reduce pulp temperature rise during exposure of intact premolars to light emitted by a high-power LED light-curing unit (LCU).
Methods and Materials:
After local Ethics Committee approval (#255945), intact, upper first premolars requiring extraction for orthodontic reasons from five volunteers received infiltrative and intraligamental anesthesia. The teeth (n=9) were isolated using rubber dam, and a minute pulp exposure was attained. The sterile probe from a wireless, NIST-traceable, temperature acquisition system was inserted directly into the coronal pulp chamber. Real-time pulp temperature (PT) (°C) was continuously monitored, while the buccal surface was exposed to a polywave LED LCU (Bluephase 20i, Ivoclar Vivadent) for 30 seconds with simultaneous application of a lingually directed air spray (30s-H/AIR) or without (30s-H), with a seven-minute span between each exposure. Peak PT values were subjected to one-way, repeated-measures analysis of variance, and PT change from baseline (ΔT) during exposure was subjected to paired Student's t-test (α=0.05).
Results:
Peak PT values of the 30s-H group were significantly higher than those of 30s-H/AIR group and those from baseline temperature (p<0.001), whereas peak PT values in the 30s-H/AIR group were significantly lower than the baseline temperature (p=0.003). The 30s-H/AIR group showed significantly lower ΔT values than did the 30s-H group (p<0.001).
Conclusion:
Applying air flow simultaneously with LED exposure prevents in vivo pulp temperature rise.
Alternative photoinitiators with different absorption wavelengths have been used in resin composites (RCs), so it is crucial to evaluate the effectiveness of light-curing units (LCUs) on these products. Objective Using Fourier transform infrared analysis (FTIR) in vitro, the effects of varying radiant exposure (RE) values generated by second and third generation LED LCUs on the degree of conversion (DC) and maximum rate of polymerization (Rpmax) of an experimental Lucirin TPO-based RC were evaluated.Material and Methods 1 mm or 2 mm thick silicon molds were positioned on a horizontal attenuated total reflectance (ATR) unit attached to an infrared spectroscope. The RC was inserted into the molds and exposed to varying REs (18, 36 and 56 J/cm2) using second (Radii Plus, SDI) and third generation LED LCUs (Bluephase G2/Ivoclar Vivadent) or a quartz tungsten based LCU (Optilux 501/SDS Kerr). FTIR spectra (n=7) were recorded for 10 min (1 spectrum/s, 16 scans/spectrum, resolution 4 cm-1) immediately after their application to the ATR. The DC was calculated using standard techniques for observing changes in aliphatic to aromatic peak ratios both prior to, and 10 min after curing, as well as during each 1 second interval. DC and Rpmax data were analyzed using 3-way ANOVA and Tukey’s post-hoc test (p=0.05).Results No significant difference in DC or Rpmax was observed between the 1 mm or 2 mm thick specimens when RE values were delivered by Optilux 501 or when the 1 mm thick composites were exposed to light emitted by Bluephase G2, which in turn promoted a lower DC when 18 J/cm2 (13 s) were delivered to the 2 mm thick specimens. Radii Plus promoted DC and Rpmax values close to zero under most conditions, while the delivery of 56 J/cm2 (40 s) resulted in low DC values.Conclusions The third generation LCU provided an optimal polymerization of Lucirin TPO-based RC under most tested conditions, whereas the second generation LED-curing unit was useless regardless of the RE.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.