Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV), a biodegradable polyester, was electrospun to form defect-free fibers with high surface-area-to-volume ratio for skin regeneration. Several parameters such as solvent ratio, polymer concentration, applied voltage, flow rate, and tip-to-target distance were optimized to achieve defect-free morphology. The average diameter of the PHBV fibers was 724 ± 91 nm. PHBV was also solvent-cast to form 2-D films, and its mechanical properties, porosity, and degradation rates were compared with PHBV fibers. Our results demonstrate that PHBV fibers exhibited higher porosity, increased ductility, and faster degradation rate when compared with PHBV 2-D films (p < 0.05). In vitro studies with PHBV fibers and 2-D films were carried out to evaluate the adhesion, viability, proliferation, and gene expression of human skin fibroblasts. Cells adhered and proliferated on both PHBV fibers and 2-D films. However, the proliferation of cells on the surface of PHBV fibers was comparable to tissue culture polystyrene (TCPS, control) (p > 0.05). The gene expression of collagen I and elastin was significantly up-regulated when compared with TCPS control, whereas collagen III was down-regulated on PHBV fibers and 2-D film after 14 days in culture. The less ductile PHBV 2-D films showed higher levels of elastin expression. Furthermore, the PHBV fibers in the presence and absence of an angiogenesis factor (R-Spondin 1) were evaluated for their wound healing capacity in a rat model. The wound contracture in R-Spondin-1-loaded PHBV fibers was found to be significantly higher when compared with PHBV fibers alone after 7 days (p < 0.05). Furthermore, the presence of fibers promoted an increase in collagen and aided re-epithelialization. Thus our results demonstrate that the topography and mechanical and chemical stimuli have a pronounced influence on the cell proliferation, gene expression, and wound healing.
Tissue engineering is an evolving multi-disciplinary field with cutting-edge technologies and innovative scientific perceptions that promise functional regeneration of damaged tissues/organs. Tissue engineered medical products (TEMPs) are biomaterial-cell products or a cell-drug combination which is injected, implanted or topically applied in the course of a therapeutic or diagnostic procedure. Current tissue engineering strategies aim at 3D printing/bioprinting that uses cells and polymers to construct living tissues/organs in a layer-by-layer fashion with high 3D precision. However, unlike conventional drugs or therapeutics, TEMPs and 3D bioprinted tissues are novel therapeutics and need different regulatory protocols for clinical trials and commercialization processes. Therefore, it is essential to understand the complexity of raw materials, cellular components, and manufacturing procedures to establish standards that can help to translate these products from bench to bedside. These complexities are reflected in the regulations and standards that are globally in practice to prevent any compromise or undue risks to patients. This review comprehensively describes the current legislations, standards for TEMPs with a special emphasis on 3D bioprinted tissues. Based on these overviews, challenges in the clinical translation of TEMPs & 3D bioprinted tissues/organs along with their ethical concerns and future perspectives are discussed.
Tetrameric peptide-based bioinks allow the printing of 3D cell-laden scaffolds under true physiological conditions avoiding harsh UV or chemical treatment.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.