Polycaprolactone (PCL), a semicrystalline linear resorbable aliphatic polyester, is a good candidate as a scaffold for bone tissue engineering, due to its biocompatibility and biodegradability. However, the poor mechanical properties of PCL impair its use as scaffold for hard tissue regeneration, unless mechanical reinforcement is provided. To enhance mechanical properties and promote osteoconductivity, hydroxyapatite (HA) particles were added to the PCL matrix: three PCL-based composites with different volume ratio of HA (13%, 20%, and 32%) were studied. Mechanical properties and structure were analysed, along with biocompatibility and osteoconductivity. The addition of HA particles (in particular in the range of 20% and 32%) led to a significant improvement in mechanical performance (e.g., elastic modulus) of scaffold. Saos-2 cells and osteoblasts from human trabecular bone (hOB) retrieved during total hip replacement surgery were seeded onto 3D PCL samples for 1-4 weeks. Following the assessment of cell viability, proliferation, morphology, and ALP release, HA-loaded PCL was found to improve osteoconduction compared to the PCL alone. The results indicated that PCL represents a potential candidate as an efficient substrate for bone substitution through an accurate balance between structural/ mechanical properties of polymer and biological activities.
Highly porous composites made up of biodegradable poly-epsilon-caprolactone (PCL) and stoichiometric hydroxyapatite (HA) particles have been developed as substrate for bone-tissue regeneration. The processing technique consists of phase inversion and particulate (salt crystals) leaching. Three different HA contents (13, 20 and 26 vol %) in PCL-based composite were considered in this study. Pore microstructure with fully interconnected network and pore sizes ranging around a few hundred of mum (macroporosity) was obtained as a result of salt particles removal by leaching process. Several microns (microporosity) porosity was also created through phase inversion of polymer solution. Total porosity up to 95% was achieved. Human marrow stromal cells (MSC) were seeded onto porous PCL-based composites for 1-5 weeks and cultured in osteogenic medium. MSC were able to adhere and grow on PCL-based substrates with a plateau at 3-4 weeks. However, the small effect of bioactive signals on the biological response evaluated in MSC cell culture suggests a prior role of topography on the biological response. Importantly, the presence of HA as a bioactive solid signal determines an increase of mechanical properties. On the overall, the results indicated that porous PCL-based composites are potential candidate for bone substitution with beneficial influence on structural characteristics by solid signal addition.
Background: Six titanium disks with six different surface treatments were examined: SS: smooth (polished) surface; TPS: plasma spray; C100: sand blasting by aluminum oxide (Al2O3) Ø 100 µm and acid etching; C150: sand blasting by Al2O3 Ø 150 µm and acid etching; B60: sand blasting by zirconium oxide (ZrO2) Ø 60 µm and acid etching; and B120: sand blasting by ZrO2 Ø 120 µm and acid etching.
Methods: The surface characteristics were determined by scanning electron microscopy (SEM) observation and a roughness tester. Raman spectroscopy was used to determine the presence of residual substances on the samples. Cells were seeded onto the disk and after 24 hours, 6 days, and 12 days were observed under SEM and growth curves generated with a cell counter. Some samples were used to determine alkaline phosphatase activity (ALP), using a colorimetric assay.
Results: SEM observation revealed drastic differences in surface microtopography, with a higher cell density on sand‐blasted and acid‐etched (SLA) samples than SS and TPS, and more regularly aligned cells on B60 and B120 surfaces than on the others. The growth curves showed a greater adhesion of cells on the etched/blasted surfaces compared to the SS and TPS surfaces. The number of cells increased on all the SLA samples, especially B60, throughout the experiment. At the same time, there was considerable ALP activity on the B60 sample, while it remained at extremely low levels on SS and TPS surfaces. Raman analyses revealed Al2O3 debris on C100 and C150, partly explaining the poorer performances of these two surface treatments, since this substance was shown to be toxic for cultured osteoblasts.
Conclusions: Surface treatments influence the growth and the metabolic activity of cultured osteoblasts, and B60 seems to be the most favorable surface inducing a more pronounced proliferation of cells together with a high differentiation degree. J Periodontol 2004;75:273‐282.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.