We report on the conduction mechanisms of novel Ru/MgO/Cu and Ru/MgO/Ta resistive switching memory (RSM) devices. Current-voltage (I–V) measurements revealed Schottky emission (SE) as the dominant conduction mechanism in the high resistance state (HRS), which was validated by varying temperatures and transmission electron microscopy (TEM) results. Retention of more than 10 years at 85 °C was obtained for both Ru/MgO/Ta and Ru/MgO/Cu RSM devices. In addition, annealing processes greatly improved the consistency of HRS and LRS switching paths from cycle to cycle, exhibiting an average ON/OFF ratio of 102. Further TEM studies also highlighted the difference in crystallinity between different materials in Ru/MgO/Cu RSM devices, confirming Cu filament identification which was found to be 10 nm in width.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.