Chitin biopolymer production and its by-product chitosan show great potential. These biomaterials have great applicability in various fields because they are non-toxic, biodegradable, biocompatible, and have antimicrobial effects. The most common source of chitin and chitosan is the crustaceous shell; however, mushrooms are an alternative source for isolating these biopolymers because their cellular wall has a high content of chitin, which may be transformed into chitosan through a deacetylation reaction. The main objective of this research was to obtain chitosan through the deacetylation of chitin isolated from the Ganoderma lucidum basidiomycetes mushroom, which is obtained through biotechnological culture. The material characterization was performed using X-ray diffraction, Fourier transform infrared spectroscopy, thermogravimetric analysis, and an evaluation of cytotoxicity comparing the results obtained with results for commercial chitosan. Protocol results showed that chitosan obtained from this mushroom had a significant similitude with commercial chitosan, yet the one obtained using P2 protocol was the one that rendered the best results: including diffractogram peaks, characteristic infrared analysis bands, and an 80.29 % degree of deacetylation. Cytotoxicity in vitro testing showed that the material was non-toxic; furthermore, it rendered very promising information regarding the evaluation of future applications of this biomaterial in the field of biomedicine.
Currently, silver nanoparticles (AgNPs) constitute an interesting field of study in medicine, catalysis, optics, among others. For this reason, it has been necessary to develop new methodologies that allow a more efficient production of AgNPs with better antimicrobial and biological properties. In this research growth time effects Anamorphous Bjerkandera sp. R1 and the silver nitrate (AgNO3) concentration over AgNPs synthesis were studied. Through the protocol used in this work, it was found that the action of the capping proteins on the surface of the mycelium played a determining role in the reduction of the Ag+ ion to Ag0 nanoparticles producing a particle size that oscillated between 10 and 100 nm. The progress of the reaction was monitored using visible UV–Vis spectroscopy and the synthesized AgNPs were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Fourier transform infrared radiation (FTIR) spectroscopy. The best synthetic properties were found at 1 mM of AgNO3 concentration, growth time of 8 days, and reaction time of 144 h. Nanometals obtention from microorganisms could be considered as a new method of synthesis, due to reducing abilities of metal ions through its enzymatic system and represents low-cost synthesis that reduces the generation of harmful toxic wastes.
The chitin was isolated from the Ganoderma lucidum submerged cultures mycelium as potential source of chitin under biotechnological processes. The extraction of chitin was carried out through 5 different assays which involved mainly three phases: pulverization of the mushroom, deproteinization of the mycelia with NaOH solution, and a process of decolorization with potassium permanganate and oxalic acid. The chitin contents extracted from 9-day mycelia were 413, 339, 87, 78, and 144 mg/g−1 (milligrams of chitin/grams of dry biomass) for A1, A2, A3, A4, and A5, respectively. Obtained chitin was characterized by X-Ray Diffraction (XRD), by Fourier transform infrared spectroscopy (FTIR), and by thermal analysis (TGA). The results showed that Ganoderma lucidum chitin has similar characteristic of chitin from different fonts. The advantage of the biotechnological processes and the fact that Ganoderma lucidum fungus may be used as a potential raw material for chitin production were demonstrated.
A combination of gel-casting and polymeric foam infiltration methods is used in this study to prepare porous bodies of hydroxyapatite (HA), to provide a better control over the microstructures of samples. These scaffolds were prepared by impregnating a body of porous polyurethane foam with slurry containing HA powder, and using a percentage of solids between 40% and 50% w/v, and three different types of monomers to provide a better performance. X-Ray Diffraction (XRD), and Fourier Transformed Infrared (FTIR) and Scanning Electron Microscopy (SEM) were employed to evaluate both the powder hydroxyapatite and the scaffolds obtained. In addition, porosity and interconnectivity measurements were taken in accordance with the international norm. Bioactivity was checked using immersion tests in Simulated Body Fluids (SBF). After the sintering process of the porous bodies, the XRD results showed peaks characteristic of a pure and crystalline HA (JCPDS 9-432) as a single phase. SEM images indicate open and interconnected pores inside the material, with pore sizes between 50 and 600 μm. Also, SEM images demonstrate the relatively good bioactivity of the HA scaffolds after immersion in SBF. All results for the porous HA bodies suggest that these materials have great potential for use in tissue engineering.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.