Thiol group functionalized silica-coated magnetic nanoparticles (Si-MNPs@SH) were synthesized for rapid and selective magnetic field-based separation of mixed proteins. The highest adsorption efficiencies of binary proteins, bovine serum albumin (BSA; 66 kDa; pI = 4.65) and lysozyme (LYZ; 14.3 kDa; pI = 11) were shown at the pH values corresponding to their own pI in the single-component protein. In the mixed protein, however, the adsorption performance of BSA and LYZ by Si-MNPs@SH was governed not only by pH but also by the molecular weight of each protein in the mixed protein.
Zirconium based thin film have been deposited by atomic layer deposition (ALD) process using Zr and Si containing Zr precursor with ozone as oxidant. We have pursued a means to control composition by varying Zr and Si containing precursor by cycle frequency. The molar ratio of Si to Zr in the Zr based films was 0.2, 0.25, 0.33, and 0.5. Addition of Si containing Zr precursor on Zirconium based thin films was effective for the decrease of the roughness, while an increase of density. XPS analysis indicated that the addition of Si containing Zr precursors in the Zr based film formed the silicate structure. The XRD analysis of the all ZrO2-SiO2 mixed films annealed at 600 degrees C for 5 min indicated the presence of amorphous. However, the ZrO2 film showed diffraction peaks at 2θ = 30.6 degrees due to the presence of the Tetragonal ZrO2. The incorporation of Si into ZrO2 films helps stabilize an amorphous structure during deposition and annealing. The Zr based thin film (Si/Zr = 0.25) exhibited that the leakage current density was 6.2 x 10(-7) A/cm2 at a bias of - 1.5 V.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.