Metallic lithium (Li) and sodium (Na) anodes have received great attention as ideal anodes to meet the needs for high energy density batteries due to their highest theoretical capacities. Although many approaches have successfully improved the performances of Li or Na metal anodes, many of these methods are difficult to scale up and thus cannot be applied in the production of batteries in practice. In this work, we introduce nanocrevasses in a carbon fiber scaffold which can facilitate the penetration of molten alkali metal into a carbon scaffold by enhancing its wettability for Li/Na metal. The resulting alkali metal/carbon composites exhibit stable long-term cycling over hundreds of cycles. The facile synthetic method is enabled for scalable production using recycled metal waste. Thus, the addition of nanocrevasses to carbon fiber as a scaffold for alkali metals can generate environmentally friendly and cost-effective composites for practical electrode applications.
MnO2 is shown for the first time to be electrochemically active as a conversion anode for Na-ion batteries (NIBs). Space-confined ultrafine (UF)-MnO2, with an average crystal size of 4 nm, synthesized using a porous silicon dioxide templated hydrothermal process exhibits a high reversible sodiation capacity of 567 mA h g(-1), in contrast to the negligible activity shown by the aggregates of larger (14 nm) MnO2 nanocrystallites. The remarkably enhanced sodiation activity of the UF-MnO2 is attributable to its greatly reduced crystal size, which facilitates diffusion of Na ions, along with high surface energy arising from extensive heterogeneous interfacial bonding with the SiO2 surrounding. The UF-MnO2 anode exhibits an exceptional rate and cycle performance, exhibiting >70% capacity retention after 500 cycles. In operando synchrotron X-ray absorption near-edge structural analysis reveals combined charge-storage mechanisms involving conversion reaction between Mn(III) and Mn(II) oxides, Mn(III)-O1.5 + Na(+) + e(-)- ↔ 1/2Na2O + Mn(II)-O, and non-Mn-centered redox reactions. The finding suggests a new strategy for "activating" the potential electrochemical electrode materials that appear inactive in the bulk form.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.