Pure phase Y3Fe5O12 (YIG) ceramics was successfully produced by tape-casting forming process and one-step solid-state reaction method. With the sintering temperature above 1100 ºC, the pure phase YIG ceramics was synthesized with no YIP or Fe2O3 phase in XRD patterns. YIG ceramic sintering at 1400 ºC for 10 h showed a clear grain structure with an obvious grain boundary, and no pores were observed in the SEM images. YIG ceramics in this paper has a high relative density which was 99.8% and the saturation magnetization was 28.2 emu/g at room temperature. The hysteresis loss at temperatures of 230-360 K was smaller than 10 mJ/kg. The tan Se was nearly zero at 6~7 GHz and 11~12 GHz, showing that it can be used as a good material for microwave applications. In addition, the low values of tan and tan indicates that it may have a good electromagnetic wave absorption ability.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.