Manufactured sand (MS) has been started utilizing as an alternative in constructions due to the escalated demand for river sand (RS). The microfine aggregate (MFA) is a salient constituent in manufactured sand, which is a crushed reactive form of parent rocks having particles less than 0.075 mm. This paper presents the effects of varying microfine aggregate levels on bleeding, plastic shrinkage cracking (PSC) and compressive strength of MS made concrete. Two types of MS were utilized: MS from Hornblende‐Gneiss rock (MH) and MS from Charnockite rock (MC) and the MFA level was ranged from 0% to 12% at 3% increments and the reference concrete was prepared with RS alone. With the MFA levels, the bleeding of MS concretes was reduced where, at 0% MFA level the maximum bleeding rates were observed for MC (1.63 kg/m2) and MH (0.84 kg/m2) concretes. PSC results were analyzed from an image processing technique, which revealed an increasing trend of mean and maximum crack widths, crack length and crack area with the MFA levels. At 0% MFA, the mean crack width of MC (0.19 mm) and MH (0.17 mm) concretes manifested marginally similar to RS concrete (0.17 mm). The decreasing bleeding with the MFA levels can be attributed to the increasing severity to PSC. Moreover, the optimum 28 days compressive strength of MC (57.5 MPa) and MH (56.1 MPa) concretes was achieved at 3% MFA level which are higher than RS concrete (51.5 MPa). Consequently, the MFA level should be limited to 3% for better plastic and hardened performance of MS made concrete.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.