Three-dimensional (3D) bioprinting technology has put forward a great deal of interest in the current time by facilitating easy adaptability in many industries and research sectors such as biomedical, manufacturing,...
The article discusses the influence of the post-process on the mechanical properties of elements produced with the use of the mask stereolithography (mSLA) method. Printed samples were subjected to the following post-process steps: Washing and post-curing, at various times. Then, static tensile and static bending tests were carried out, as well as Shore D hardness measurements for the inner and surface part of the sample, as well as profilographometric analysis of the surface. The post-curing time has been found to strongly affect the tensile and bending strength of printouts, and to improve their surface quality. Washing has an ambiguous effect on the strength of the printouts, but, in the end, it was found that extended washing slightly reduces the strength. Washing significantly affects the quality of the printout surface. A washing time that is too short results in a surface that strongly resembles the printing process, with high roughness. Increasing the washing time to 10 min lowers the roughness by one order of magnitude. Post-curing has also been shown to be beneficial for the cured sample with the application of shielding water. This approach results in an improvement in the flexural strength of the printouts. In general, the obtained research results indicate that, for printouts with cross-sectional dimensions of several mm, the optimal washing time is no more than 10 min and the post-curing time is at least 30 min.
The nanorods of bismuth sulfoiodide (BiSI) were synthesized at relatively low temperature (393 K) through a wet chemical method. The crystalline one-dimensional (1D) structure of the BiSI nanorods was confirmed using high resolution transmission microscopy (HRTEM). The morphology and chemical composition of the material were examined by applying scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS), respectively. The average diameter of 126(3) nm and length of 1.9(1) µm of the BiSI nanorods were determined. X-ray diffraction (XRD) revealed that prepared material consists of a major orthorhombic BiSI phase (87%) and a minor amount of hexagonal Bi13S18I2 phase (13%) with no presence of other residual phases. The direct energy band gap of 1.67(1) eV was determined for BiSI film using diffuse reflectance spectroscopy (DRS). Two types of photodetectors were constructed from BiSI nanorods. The first one was traditional photoconductive device based on BiSI film on stiff glass substrate equipped with Au electrodes. An influence of light intensity on photocurrent response to monochromatic light (λ = 488 nm) illumination was studied at a constant bias voltage. The novel flexible photo-chargeable device was the second type of prepared photodetectors. It consisted of BiSI film and gel electrolyte layer sandwiched between polyethylene terephthalate (PET) substrates coated with indium tin oxide (ITO) electrodes. The flexible self-powered BiSI photodetector exhibited open-circuit photovoltage of 68 mV and short-circuit photocurrent density of 0.11 nA/cm2 under light illumination with intensity of 0.127 W/cm2. These results confirmed high potential of BiSI nanorods for use in self-powered photodetectors and photo-chargeable capacitors.
The dynamic development of flexible wearable electronics creates new possibilities for the production and use of new types of sensors. Recently, polymer nanocomposites have gained great popularity in the fabrication of sensors. They possess both the mechanical advantages of polymers and the functional properties of nanomaterials. The main drawback of such systems is the complexity of their manufacturing. This article presents, for the first time, fabrication of an antimony sulfoiodide (SbSI) and polyurethane (PU) nanocomposite and its application as a piezoelectric nanogenerator for strain detection. The SbSI/PU nanocomposite was prepared using simple, fast, and efficient technology. It allowed the obtainment of a high amount of material without the need to apply complex chemical methods or material processing. The SbSI/PU nanocomposite exhibited high flexibility and durability. The microstructure and chemical composition of the prepared material were investigated using scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS), respectively. These studies revealed a lack of defects in the material structure and relatively low agglomeration of nanowires. The piezoelectric response of SbSI/PU nanocomposite was measured by pressing the sample with a pneumatic actuator at different excitation frequencies. It is proposed that the developed nanocomposite can be introduced into the shoe sole in order to harvest energy from human body movement.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.