Background
Biodegradable polyurethanes have found widespread use in soft tissue engineering due to their suitable mechanical properties and biocompatibility.
Methods
In this study, polyurethane samples were synthesized from polycaprolactone, hexamethylene diisocyanate, and a copolymer of 1,4-butanediol as a chain extender. Polyurethane scaffolds were fabricated by a combination of liquid–liquid phase separation and salt leaching techniques. The effect of the NCO:OH ratio on porosity content and pore morphology was investigated.
Results
Scanning electron micrographs demonstrated that the scaffolds had a regular distribution of interconnected pores, with pore diameters of 50–300 μm, and porosities of 64%–83%. It was observed that, by increasing the NCO:OH ratio, the average pore size, compressive strength, and compressive modulus increased. L929 fibroblast and chondrocytes were cultured on the scaffolds, and all samples exhibited suitable cell attachment and growth, with a high level of biocompatibility.
Conclusion
These biodegradable polyurethane scaffolds demonstrate potential for soft tissue engineering applications.
In this study, new nano-fluor-hydroxyapatite (nFHA)/polyurethane composite scaffolds were fabricated for potential use in bone tissue engineering. Polyester urethane samples were synthesized from polycaprolactone, hexamethylene diisocyanate, and 1,4-butanediol as chain extender. Nano fluor-hydroxyapatite (nFHA) was successfully synthesized by sol-gel method. The solid–liquid phase separation and solvent sublimation methods were used for preparation of the porous composites. Mechanical properties, chemical structure, and morphological characteristics of the samples were investigated by compressive test, Fourier transform infrared, and scanning electron microscopy (SEM) techniques, respectively. The effect of nFHA powder content on porosity and pore morphology was investigated. SEM images demonstrated that the scaffolds were constituted of interconnected and homogeneously distributed pores. The pore size of the scaffolds was in the range 50–250 μm. The result obtained in this research revealed that the porosity and pore average size decreased and compressive modulus increased with nFHA percentage. Considering morphological, physical, and mechanical properties, the scaffold with a higher ratio of nFHA has suitable potential use in tissue regeneration.
In this study, grafted gelatin with oligoaniline (GelOA) was synthesized and then mixed with Poly (vinyl alcohol) (PVA). Several scaffolds with different ratio of PVA/GelOA were electrospun to fabricate electroactive scaffolds. GelOA was characterized using Fourier‐transform infrared spectroscopy (FTIR); moreover, nanofiber properties were evaluated by differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), and scanning electron microscope (SEM) analyses. Nanofibers diameter was decreased with aniline oligomer increment form 300 to 150 nm because of the hydrophobic nature of the aniline oligomer. Aniline oligomer electroactivity was studied using cyclic voltammetry, which exhibited two redox peaks at 0.4 and 0.6. Moreover, aniline oligomer enhancement resulted in melting point increasing from 220°C to 230°C because of the crystallinity increment. To assess the biocompatibility of nanofibers, cell viability and cell adhesion were tracked using mesenchymal stem cell (MSCs). It was revealed that the presence of aniline oligomer leads to enhancing the conductivity, thermal properties and lowering the degradation rate and drug release. Among of different scaffolds, sample with high content of GelOA shows better behavior in physical and biological properties. Accumulative drug releases under applied electrical field at 40 minutes showed that the drug release for stimulated condition is about 33% more than the unapplied electrical field one.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.