Environment-friendly nanosponges, having a high content of carboxyl groups, were synthesized by crosslinking β-cyclodextrin and linecaps, a highly soluble pea starch derivative, with citric acid in water. Additionally, pyromellitic nanosponges were prepared by reacting β-cyclodextrin and linecaps with pyromellitic dianhydride in dimethyl sulfoxide and used in comparison with the citric nanosponges. After ion-exchange of the carboxyl groups H+ with sodium ions, the ability of the nanosponges to sequester heavy metal cations was investigated. At a metal concentration of 500 ppm, the pyromellitate nanosponges exhibited a higher retention capacity than the citrate nanosponges. At lower metal concentrations (≤50 ppm) both the citrate and the pyromellitate nanosponges showed high retention capacities (up to 94% of the total amount of metal), while, in the presence of interfering sea water salts, the citrate nanosponges were able to selectively adsorb a significantly higher amount of heavy metals than the pyromellitate nanosponges, almost double in the case of Cu2+.
A new magnetic nanocomposite called MIL-100(Fe) @Fe3O4@AC was synthesized by the hydrothermal method as a stable adsorbent for the removal of Rhodamine B (RhB) dye from aqueous medium. In this work, in order to increase the carbon uptake capacity, magnetic carbon was first synthesized and then the Fe3O4 was used as the iron (III) supplier to synthesize MIL-100(Fe). The size of these nanocomposite is about 30–50 nm. Compared with activated charcoal (AC) and magnetic activated charcoal (Fe3O4@AC) nanoparticles, the surface area of MIL-100(Fe) @Fe3O4@AC were eminently increased while the magnetic property of this adsorbent was decreased. The surface area of AC, Fe3O4@AC, and MIL-100(Fe) @Fe3O4@AC was 121, 351, and 620 m2/g, respectively. The magnetic and thermal property, chemical structure, and morphology of the MIL-100(Fe) @Fe3O4@AC were considered by vibrating sample magnetometer (VSM), thermogravimetric analysis (TGA), zeta potential, X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), Brunner-Emmet-Teller (BET), and transmission electron microscopy (TEM) analyses. The relatively high adsorption capacity was obtained at about 769.23 mg/g compared to other adsorbents to eliminate RhB dye from the aqueous solution within 40 min. Studies of adsorption kinetics and isotherms showed that RhB adsorption conformed the Langmuir isotherm model and the pseudo second-order kinetic model. Thermodynamic amounts depicted that the RhB adsorption was spontaneous and exothermic process. In addition, the obtained nanocomposite exhibited good reusability after several cycles. All experimental results showed that MIL-100(Fe) @Fe3O4@AC could be a prospective sorbent for the treatment of dye wastewater.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.