The aim of this study was to determine the effect of sandblasting and electrical discharge machining (EDM) on cast and machined titanium surfaces and titanium-porcelain adhesion. Twenty machined titanium specimens were prepared by manufacturer (groups 1 and 2). Thirty specimens were prepared with autopolymerizing acrylic resin. Twenty of these specimens (groups 3 and 4) were cast with commercially pure titanium and the alpha-case layer was removed. For control group (group 5), 10 specimens were cast by using NiCr alloy. Groups 2 and 4 were subjected to EDM while groups 1, 3, and 5 were subjected to sandblasting. Surface examinations were made by using a scanning electron microscope (SEM). A low-fusing porcelain was fused on the titanium surfaces, whereas NiCr specimens were covered using a conventional porcelain. Titanium-porcelain adhesion was characterized by a 3-point bending test. Results were analyzed by Kruskal-Wallis and Mann-Whitney U tests. Metal-porcelain interfaces were characterized by SEM. The bond strength of control group was higher than that of the titanium-porcelain system. There was no significant difference between cast and machined titanium groups (p > 0.05). There was no significant difference between EDM and sandblasting processes (p > 0.05). The use of EDM as surface treatment did not improve titanium-porcelain adhesion compared with sandblasting.
The aim of this study was to determine the effect of airborne-particle abrasion (APA), sodium hydroxide anodization (SHA), and electrical discharge machining (EDM) on cast titanium surfaces and titanium-porcelain adhesion. Ninety titanium specimens were cast with pure titanium and the alpha-case layer was removed. Specimens were randomly divided into three groups. Ten specimens from each group were subjected to APA. SHA was applied to the second subgroups, and the remaining specimens were subjected to the EDM. For the control group, 10 specimens were cast using NiCr alloy and subjected to only APA. Surfaces were examined by using scanning electron microscope and a surface profilometer. Three titanium porcelains were fused on the titanium surfaces, whereas NiCr specimens were covered with conventional porcelain. Titanium-porcelain adhesion was characterized by a 3-point bending test. Statistical analysis showed that the porcelain-metal bond strength of the control group was higher than that of the titanium-porcelain system (p < 0.05). There were no significant differences between the bond strengths of titanium groups (p 0.05), except the bond strengths of Noritake Super Porcelain TI-22 groups on which APA and SHA were applied (p < 0.05). SHA and EDM as surface treatment did not improve titanium-porcelain adhesion when compared to APA.
Background. The surface properties of implants are effective factors for increasing the osseointegration and activity of osteoprogenitor cells. This study compared the stability of dental implants with sandblasted and acid-etched (SLA) and modified surfaces (SLActive) using the resonance frequency analysis (RFA). Methods. In a split-mouth design, 50 dental implants with either SLA surface properties (n=25) or modified (SLActive) surface properties (n=25) were placed in the mandibles of 12 patients with a bilateral posterior edentulous area. Implant stability was measured using RFA (Osstell) at implant placement time and every week for 1, 2, and 3 months before the conventional loading time. Results. One week following the implantation, implant stability increased from 70 to 77.67 for SLA and from 71.67 to 79 for SLActive (P<0.05). Stability improved each week except in the 4th week in SLActive surface measurements. No significant differences were observed between the groups at 2 and 3 months (P>0.05). Conclusions. For both implant surfaces, increased stability was observed over time, with no significant differences between the groups.
Objective: The aim of this study was to compare the effects of different surface treatments on the elemental composition stability of as-received and recast types of NiCr casting alloys. Material and Methods: Six commercial NiCr dental casting alloys (Kera N, Nodelco, Bellabond, Wiron 99, Metaplus VK, and Tritech D) were used in this study. Seventy-two specimens (12 × 12 × 1.2 mm) were produced using the lost-wax casting process. Three casting protocols were established in relation to the proportion of as-received and recast alloys: Group A (100% as-received metal), Group B (50 wt% new metal, 50 wt% once-recast metal), and Group C (100% once-recast metal). Two specimens in every group received two different surface treatments: sandblasting with 110 µmm Al2O3 or oxidation firing. An elemental analysis was performed with x-ray energy-dispersive spectroscopy. Results were subjected to one-way analysis of variance and Tukey HSD tests. Results: The elemental composition was significantly different in the casting groups and treatment groups (<i>p</i> < 0.05). The lowest mean weight percentage Ni value was recorded for Group C and the highest for Group A. Aluminum-oxide sandblasting of the alloy surface reduced the mean weight percentage for Cr. Conclusion: Recasting metal alloys may adversely affect surface quality
In this study, embryotoxic effects of five commercially available dental alloys were investigated by using fertilized hens' eggs. One sample of each alloy was conditioned in one of the conditioning media, physiological saline (PS), 0.1 M phosphate-buffered saline (PBS, pH 7.4), and 0.1 M protein (3% bovine serum albumin, BSA) containing PBS (pH 6.8), respectively. The test solutions were injected into the fertilized hen's eggs via air sac at the beginning of the incubation. Various concentrations of a highly embryotoxic substance, AFB1, was also used as positive control test material. Mortality of the AFB1 treatment groups increased with increasing concentrations of AFB1 and the mortality values were significantly (p < 0.05) higher than those of the controls and eluent injected groups. The eluents of five commercially available dental alloys tested in the study did not have significant embryotoxic effects. Cu- and Pd-containing alloys displayed relatively high but statistically insignificant embryotoxic effects. Chick embryo might be used in determination of the embryotoxic effects of the dental alloys with its several advantages. Nevertheless, the test should be further standardized and new methods such as micronucleus test showing possible genotoxic effects of the materials should be used.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.