Our aim was to test cell and trabecular responses to mechanical loading in vitro in a tissue bone explant culture model. The ZetOS TM system provides the ability to exert cyclic compression on cancellous bone cylinders (bovine sternum) cultured in forced flow circumfusion chambers, and allows assessing mechanical parameters of the cultivated samples. We evaluated bone cellular parameters through osteocyte viability test, gene and protein expression and histomorphometric bone formation rate, in non-loaded versus loaded samples. The microarchitecture of bone cores was appraised by in vivo micro-CT imaging. After 3 weeks, the samples receiving daily cyclic compression exhibited increased osteoblast differentiation and activity associated with thicker, more plate-like shaped trabeculae, higher Young's Modulus and ultimate force as compared to unloaded samples. Osteoclast activity was not affected by mechanical strain, although it was responsive to drug treatments (retinoic acid and bisphosphonate) during the first 2 weeks of culture. Thus, in the ZetOS TM apparatus, we reproduce in vitro the osteogenic effects of mechanical strain known in vivo, making this system a unique and an essential laboratory aid for ex vivo testing of lamellar bone remodelling.

Bone quality is an important concept to explain bone fragility in addition to bone mass. Among bone quality factors, microdamage which appears in daily life is thought to have a marked impact on bone strength and plays a major role in the repair process. The starting point for all studies designed to further our understanding of how bone microdamage initiate or dissipate energy, or to investigate the impact of age, gender or disease, remains reliable observation and measurement of microdamage. In this study, 3D Synchrotron Radiation (SR) micro-CT at the micrometric scale was coupled to image analysis for the three-dimensional characterization of bone microdamage in human trabecular bone specimens taken from femoral heads. Specimens were imaged by 3D SR micro-CT with a voxel size of 1.4 µm. A new tailored 3D image analysis technique was developed to segment and quantify microcracks. Microcracks from human trabecular bone were observed in different tomographic sections as well as from 3D renderings. New 3D quantitative measurements on the microcrack density and morphology are reported on five specimens. The 3D microcrack density was found between 3.1 and 9.4/mm3 corresponding to a 2D density between 0.55 and 0.76 /mm2. The microcrack length and width measured in 3D on five selected microcrack ranged respectively from 164 µm to 209 µm and 100 µm to 120 µm. This is the first time that various microcracks in unloaded human trabecular bone - from the simplest linear crack to more complex cross-hatch cracks - have been examined and quantified by 3D imaging at this scale. The suspected complex morphology of microcracks is here considerably more evident than in the 2D observations. In conclusion, this technique opens new perspective for the 3D investigation of microcracks and the impact of age, disease or treatment.

The femtosecond laser processing enabled the structuring of six types of surfaces on titanium-6aluminium-4vanadium (Ti-6Al-4V) plates. The obtained hierarchical features consisted of a combination of microgrooves and oriented nanostructures. By adjusting beam properties such as laser polarization, the width of the microgrooves (20 or 60 μm) and the orientation of the nanostructures (parallel or perpendicular to the microgrooves) can be precisely controlled. Mesenchymal stem cells (MSCs) grown on these structured surfaces produced cytoplasmic extensions with focal contacts, while on the smooth titanium, the cells were found to be well spread and without any focal contact 12 h postseeding. The 600-nm wide nanostructures on their own were sufficient to orient the MSCs. For the multiscale structured areas, when the orientation of the nanostructures was orthogonal in relation to the microgrooves, there was an important decrease in or even a loss of cell alignment signifying that cells were sensitive to the directional nanostructures in the microgrooves. At 7 days, cell proliferation was not affected but the direction of nanostructures controlled the matrix organization. The ultrafast laser, as a new method for producing micro-nanohybrid surfaces, is a promising approach to promote desired tissue organization for tissue engineering.