No abstract

No abstract

In this study, acrylonitrile butadiene styrene (ABS) and graphite powder—a solid lubricant—were filled and characterized for friction and wear responses. The fused deposition modeling (FDM) technique was utilized to synthesize ABS–graphite composites. A twin-screw extrusion approach was employed to create the composite filament of graphite–ABS that is suitable for the FDM process. Three graphite particle ratios ranging from 0% to 5% were explored in the ABS matrix. The wear and friction properties of ABS composites were examined using a pin on disc tribometer at varied sliding velocities and weights. As a result of the graphite addition in the ABS matrix, weight losses for FDM components as well as a decreased coefficient of friction were demonstrated. Furthermore, as the graphite weight percentage in the ABS matrix grows the value of friction and wear loss decreases. The wear mechanisms in graphite filled ABS composites and ABS were extensively examined using scanning electron microscopy and confocal microscopy.

No abstract

No abstract

One of the most promising and widely used additive manufacturing technologies, fused deposition modelling (FDM), is based on material extrusion and is most commonly used for producing thermoplastic parts for functional applications with the objectives of low cost, minimal waste and ease of material conversion. Considering that pure thermoplastic materials have a significantly poor mechanical performance, it is necessary to enhance the mechanical properties of thermoplastic parts generated using FDM technology. One of the conceivable techniques is to incorporate reinforcing materials such as short glass fibre (SGF) into the thermoplastic matrix in order to produce a polymer composite that can be used in engineering applications, such as structural applications. The morphological and mechanical properties of SGF (short glass fibre) reinforced ABS- (Acrylonitrile Butadiene Styrene) based polymer composites created via the method of FDM (fused deposition modelling) were investigated in this work. Properties were evaluated at three different weight percentages (0, 15 and 30 wt%). The composite filaments were developed using the process of twin screw extrusion. The comparison was made between ABS + SGF (short glass fibre) composites and pure ABS of mechanical properties that include surface roughness, tensile strength and low-velocity impact. The tests were carried out to analyze the properties as per ASTM standards. It has been found that the impact strength and tensile strength show an improvement in glass fibre inclusion; moreover, alongside the direction of build, the surface roughness had been reduced. The studies also focused on studying the dispersion characters of SGF in ABS matrix and its impact on the properties. Strength and modulus of SGF reinforced ABS composite has been significantly improved along with reduction of ductility. A 57% increase in tensile strength has been noted for 30 wt% addition of SGF to ABS in comparison to pure ABS. It was also interesting to note the reduction in surface roughness with every incremental addition of SGF to ABS. A 40% reduction in surface roughness has been observed with a 30 wt% addition of SGF to ABS in comparison to pure ABS.

Flax is a commercial crop grown in many parts of the world both for its seeds and for its fibers. The seed-based flax variety (linseed) is considered less for its fiber after the seed is extracted. In this study, linseed straw was utilized and processed to extract fiber and cellulose through optimization of retting time and a multi-step alkaline peroxide extraction process using the Taguchi design of experiment (DOE). Effects of retting duration on fiber properties as well as effects of solvent concentration, reaction temperature, and time on removal of non-cellulosic fiber components were studied using the gravimetric technique, Fourier transform infrared (FTIR) spectroscopy and thermal studies. Based on these findings, retting for 216 h at room temperature should offer adequate retting efficiency and fiber characteristics; 70% cellulose yield was extracted successfully from linseed straw fiber using 75% ethanol–toluene at 98 °C for 4 h, 6% NaOH at 75 °C for 30 min, and 6% H2O2 at 90 °C for 120 min.

No abstract