Wire Cut Electric Discharge Machining (WCEDM) is a novel method for machining different materials with application of electrical energy by the movement of wire electrode. For this work, an AZ61 magnesium alloy with reinforcement of boron carbide and silicon carbide in different percentage levels was used and a plate was formed through stir casting technique. The process parameters of the stir casting process are namely reinforcement %, stirring speed, time of stirring, and process temperature. The specimens were removed from the casted AZ61 magnesium alloy composites through the Wire Cut Electric Discharge Machining (WCEDM) process, the material removal rate and surface roughness vales were carried out creatively. L 16 orthogonal array (OA) was used for this work to find the material removal rate (MRR) and surface roughness. The process parameters of WCEDM are pulse on time (105, 110, 115 and 120 µs), pulse off time (40, 50, 60 and 70 µs), wire feed rate (2, 4, 6 and 8 m/min), and current (3, 6, 9 and 12 Amps). Further, this study aimed to estimate the maximum ultimate tensile strength and micro hardness of the reinforced composites using the Taguchi route.
The choice of suitable inoculants in the grain refinement process and subsequent enhancement of the characteristics of the composites developed is an important materials research topic, having wide scope. In this regard, the present work is aimed at finding the appropriate composition and size of fly ash as inoculants for grain refinement of the aluminum AA 5083 composites. Fly ash particles, which are by products of the combustion process in thermal power plants, contributing to the large-scale pollution and landfills can be effectively utilized as inoculants and interatomic lubricants in the composite matrix–reinforcement subspaces synthesized in the inert atmosphere using ultrasonic assisted stir casting setup. Thus, the work involves the study of the influence of percentage and size of the fly ash dispersions on the tensile and impact strength characteristics of the aluminum AA 5083/7.5SiC composites. The C type of fly ash with the particle size in the series of 40–75 µm, 76–100 µm, and 101–125 µm and weight % in the series of 0.5, 1, 1.5, 2, and 2.5 are selected for the work. The influence of fly ash as distinct material inoculants for the grain refinement has worked out well with the increase in the ultimate tensile strength, yield strength, and impact strength of the composites, with the fly ash as material inoculants up to 2 wt. % beyond which the tensile and impact characteristics decrease due to the micro coring and segregation. This is evident from the microstructural observations for the composite specimens. Moreover, the role of fly ash as material inoculants is distinctly identified with the X-Ray Diffraction (XRD) for the phase and grain growth epitaxy and the Energy Dispersive Spectroscopy (EDS) for analyzing the characteristic X-Rays of the fly ash particles as inoculant agents in the energy spectrum.
In this paper, Al-Fe-Si-Zn-Cu (AA8079) matrix composites with several weight percentages of B4C (0, 5, 10, and 15) were synthesized by powder metallurgy (PM). The essential amount of powders was milled to yield different compositions such as AA8079, AA8079-5 wt.%B4C, AA8079-10 wt.%B4C, and AA8079-15 wt.%B4C. The influence of powder metallurgy parameters on properties’ density, hardness, and compressive strength was examined. The green compacts were produced at three various pressures: 300 MPa, 400 MPa, and 500 MPa. The fabricated green compacts were sintered at 375 °C, 475 °C, and 575 °C for the time period of 1, 2 and 3 h, respectively. Furthermore, the sintered samples were subjected to X-ray diffraction (XRD) analysis, Energy Dispersive Analysis (EDAX), and Scanning Electron Microscope (SEM) examinations. The SEM examination confirmed the uniform dispersal of B4C reinforcement with AA8079 matrix. Corrosion behavior of the composites samples was explored. From the studies, it is witnessed that the rise in PM process parameters enhances the density, hardness, compressive strength, and corrosion resistance.
This paper investigates the physical and mechanical properties of bighorns of Deccani breed sheep native from Karnataka, India. The exhaustive work comprises two cases. First, rehydrated (wet) and ambient (dry) conditions, and second, the horn coupons were selected for longitudinal and lateral (transverse) directions. More than seventy-two samples were subjected to a test for physical and mechanical property extraction. Further, twenty-four samples were subjected to physical property testing, which included density and moisture absorption tests. At the same time, mechanical testing included analysis of the stress state dependence with the horn keratin tested under tension, compression, and flexural loading. The mechanical properties include the elastic modulus, yield strength, ultimate strength, failure strain, compressive strength, flexural strength, flexural modulus, and hardness. The results showed anisotropy and depended highly on the presence of water content more than coupon orientation. Wet conditioned specimens had a significant loss in mechanical properties compared with dry specimens. The observed outcomes were shown at par with results for yield strength of 53.5 ± 6.5 MPa (which is better than its peers) and a maximum compressive stress of 557.7 ± 5 MPa (highest among peers). Young’s modulus 6.5 ± 0.5 GPa and a density equivalent to a biopolymer of 1.2 g/cc are expected to be the lightest among its peers; flexural strength 168.75 MPa, with lowest failure strain percentage of 6.5 ± 0.5 and Rockwell hardness value of 60 HRB, seem best in the class of this category. Simulation study identified a suitable application area based on impact and fatigue analysis. Overall, the exhaustive experimental work provided many opportunities to use this new material in various diversified applications in the future.
Membrane-type acoustic metamaterial (MAM) has exhibited superior sound isolation properties, as well as thin and light characteristics. However, the anti-resonance modes of traditional MAMs are generated intermittently in a wide frequency range causing discontinuities in the anti-resonance modes. Achieving broadband low-frequency sound attenuation with lightweight MAM design is still a pivotal research aspect. Here, we present a strategy to realize wide sound-attenuation bands in low frequency range by introducing the design concept of bionic configuration philosophy into the MAM structures. Built by a polymeric membrane and a set of resonators, two kinds of MAM models are proposed based on the insight of a spider web topology. The sound attenuation performance and physical mechanisms are numerically and experimentally investigated. Multi-state anti-resonance modes, induced by the coupling of the bio-inspired arrangement and the host polymer film, are systematically explored. Significant sound attenuation is numerically and experimentally observed in both the lightweight bio-inspired designs. Remarkably, compared with a traditional MAM configuration, a prominent enhancement in both attenuation bandwidth and weight-reduction performance is verified. In particular, the bio-inspired MAM Model I exhibits a similar isolation performance as the reference model, but the weight is reduced by nearly half. The bio-inspired Model II broadens the sound attenuation bandwidth greatly; meanwhile, it retains a lighter weight design. The proposed bio-inspired strategies provide potential ways for designing sound isolation devices with both high functional and lightweight performance.
Nano aluminum oxide was prepared by the combustion method using aluminum nitrate as the oxidizer and urea as a fuel. Characterization of synthesized materials was performed using SEM (scanning electron microscope), powder XRD (X-ray diffraction), FTIR (Fourier transform infrared spectroscopy), and TEM (transmission electron microscope). Al-Mg/Al2O3 (2, 4, 6, and 8 wt%) metal matrix nanocomposites were prepared by liquid metallurgy route-vertex technique. The homogeneous dispersion of nano Al2O3 particles in Al-Mg/Al2O3 metal matrix nanocomposites (MMNCs) was revealed from the field emission SEM analysis. The reinforcement particles present in the matrix were analyzed through energy-dispersive X-ray spectroscopy method. The properties (corrosion and mechanical) of the fabricated composites were evaluated. The mechanical and corrosion properties of the prepared nanocomposites initially increased and then decreased with the addition of nano Al2O3 particles in Al-Mg Matrix. The studies show that, the presence of 6 wt% of nano Al2O3 particles in the matrix improved the properties of other combinations of nano Al2O3 in the Al-Mg matrix material. Further, the Al-Mg/Al2O3 (6 wt%) MMNCs are joined by friction stir welding and evaluated for microstructural, mechanical, and corrosion properties. Al-Mg/Al2O3 MMNCs may find applications in the marine field. The response surface method (RSM) was used for the optimization of tensile strength, Young’s modulus, and microhardness of the synthesized material which resulted in a 95% of statistical confidence level. Artificial neural network (ANN) analysis was also carried out which perfectly predicted these two properties. The ANN model is optimized to obtain 99.9% accurate predictions by changing the number of neurons in the hidden layer.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.