Currently, superparamagnetic functionalized systems of magnetite (Fe3O4) nanoparticles (NPs) are promising options for applications in hyperthermia therapy, drug delivery and diagnosis. Fe3O4 NPs below 20 nm have stable single domains (SSD), which can be oriented by magnetic field application. Dispersion of Fe3O4 NPs in silicon dioxide (SiO2) matrix allows local SSD response with uniaxial anisotropy and orientation to easy axis, 90° <001> or 180° <111>. A successful, easy methodology to produce Fe3O4 NPs (6–17 nm) has been used with the Stöber modification. NPs were embedded in amorphous and biocompatible SiO2 matrix by mechanical stirring in citrate and tetraethyl orthosilicate (TEOS). Fe3O4 NPs dispersion was sampled in the range of 2–12 h to observe the SiO2 matrix formation as time function. TEM characterization identified optimal conditions at 4 h stirring for separation of SSD Fe3O4 in SiO2 matrix. Low magnetization (Ms) of 0.001 emu and a coercivity (Hc) of 24.75 Oe indicate that the embedded SSD Fe3O4 in amorphous SiO2 reduces the Ms by a diamagnetic barrier. Magnetic force microscopy (MFM) showed SSD Fe3O4 of 1.2 nm on average embedded in SiO2 matrix with uniaxial anisotropy response according to Fe3+ and Fe2+ electron spin coupling and rotation by intrinsic Neél contribution.

No abstract

No abstract

In the pulsed laser deposition of thin films, plasma parameters such as energy and density of ions play an important role in the properties of materials. In the present work, cadmium telluride thin films were obtained by laser ablation of a stoichiometric CdTe target in vacuum, using two different values for: substrate temperature (RT and 200 °C) and plasma energy (120 and 200 eV). Structural characterization revealed that the crystalline phase can be changed by controlling both plasma energy and substrate temperature; which affects the corresponding band gap energy. All the thin films showed smooth surfaces and a Te rich composition.

No abstract

No abstract

CdTe:Cu films were grown by pulsed laser deposition on Corning glass slides at a substrate temperature of 300 °C. The thin films were grown using CdTe and Cu2Te powders, varying the Cu2Te concentration from 3 to 10 wt. %. The structural, compositional, optical, and electrical properties were analyzed as a function of the nominal copper concentration. X-ray diffraction shows that films have CdTe cubic phase. The compositional analysis indicates that CdTe:Cu films grown with lower Cu content have Te excess, on the other hand, films with higher Cu content have Te deficiencies. The electrical measurements showed that CdTe:Cu films grown with low Cu content present lowest resistivity.