The hydrolytic and enzymatic degradation of polymer films of poly(3-hydroxybutyrate) (PHB) of different molecular mass and its copolymers with 3-hydroxyvalerate (PHBV) of different 3-hydroxyvalerate (3-HV) content and molecular mass, 3-hydroxy-4-methylvalerate (PHB4MV), and polyethylene glycol (PHBV-PEG) produced by the Azotobacter chroococcum 7B by controlled biosynthesis technique were studied under in vitro model conditions. The changes in the physicochemical properties of the polymers during their in vitro degradation in the pancreatic lipase solution and in phosphate-buffered saline for a long time (183 days) were investigated using different analytical techniques. A mathematical model was used to analyze the kinetics of hydrolytic degradation of poly(3-hydroxyaklannoate)s by not autocatalytic and autocatalytic hydrolysis mechanisms. It was also shown that the degree of crystallinity of some polymers changes differently during degradation in vitro. The total mass of the films decreased slightly up to 8–9% (for the high-molecular weight PHBV with the 3-HV content 17.6% and 9%), in contrast to the copolymer molecular mass, the decrease of which reached 80%. The contact angle for all copolymers after the enzymatic degradation decreased by an average value of 23% compared to 17% after the hydrolytic degradation. Young’s modulus increased up to 2-fold. It was shown that the effect of autocatalysis was observed during enzymatic degradation, while autocatalysis was not available during hydrolytic degradation. During hydrolytic and enzymatic degradation in vitro, it was found that PHBV, containing 5.7–5.9 mol.% 3-HV and having about 50% crystallinity degree, presents critical content, beyond which the structural and mechanical properties of the copolymer have essentially changed. The obtained results could be applicable to biomedical polymer systems and food packaging materials.
Compositions of polylactide (PLA) and poly(3-hydroxybutyrate) (PHB) thermoplastic polyesters originated from the nature raw have been obtained by blending under shear deformations and electrospinning methods in the form of films and nanofibers as well as unwoven nanofibrous materials, respectively. The degrees of crystallinity calculated on the base of melting enthalpies and thermal transition temperatures for glassy state, cold crystallization, and melting point for individual biopolymers and ternary polymer blends PLA-PHB- poly(ethyleneglycol) (PEG) have been evaluated. It has been shown that the mechanical properties of compositions depend on the presence of plasticizers PEG with different molar masses in interval of 400–1000. The experiments on the action of mold fungi on the films have shown that PHB is a fully biodegradable polymer unlike PLA, whereas the biodegradability of the obtained composites is determined by their composition. The sorption activity of PLA–PHB nanofibers and unwoven nanofibrous PLA–PHB composites relative to water and oil has been studied and the possibility of their use as absorbents in wastewater treatment from petroleum products has been demonstrated.
The influence of small concentrations of nanoscale silicon and titanium dioxide particles on the structure, physicomechanical and sorption properties, thermal destruction resistance, and thermal and photo oxidant destruction of unwoven ultrathin fibrous materials that are prepared via electrostatic solution spin ning is studied. It is established that nanoscale particles favor the formation of thinner fibers with improved physical and mechanical parameters; good resistance to thermal, thermo and photo oxidant destruction; and positive dynamics of mesenchymal stem cells.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.