Growth, structural, optical, piezoelectric and etching analysis of L-lysine p-nitrophenolate monohydrate single crystals

Abstract

Nonlinear optical single crystals of L-lysine p-nitrophenolate monohydrate (LLPNP) were grown in aqueous solution by the slow evaporation solution technique (SEST). The grown crystals were subjected to powder X-ray diffraction analysis, (PXRD) and it was found that the title compound was crystallized in the orthorhombic crystal system with noncentrosymmetric space group of [Formula: see text]212121. The vibrational frequencies of various functional groups present in the crystal were analyzed using the FTIR spectrum with a wavenumber range between 450 cm[Formula: see text] and 4000 cm[Formula: see text]. The microhardness analysis of the sample revealed that the crystal belongs to the soft material category. Piezoelectric analysis was performed to measure the value of the piezoelectric (d[Formula: see text]) coefficient. Blue light emission of the material was confirmed using the photoluminescence spectrum. Thermal stability of the grown crystal was analyzed using a melting point apparatus and it was found that the LLPNP is stable upto 175[Formula: see text]C. Etching analysis was performed at various durations, in order to identify the surface properties of the LLPNP crystal.

An Efficient Nonlinear Optical, Magnetic Transition Metal Ion Nickel Doped L- Threonine Cadmium Acetate Monohydrate

“…The addition of Ni 2+ metal ions the sample intensity decreases, due to the shorter distance of interband metal ions. [12] This also blocking the recombination of electron-hole pairs between valance band and conduction band of Ni 2+ metal ions. Doping of Ni 2+ created an Oxygen vacancy in the crystal.…”