Characterization of Cu2ZnSnSe4 solar cells prepared from electrochemically co-deposited Cu–Zn–Sn alloy

XRD studies of an electrochemically co-deposited Cu–Zn–Sn precursor and formation of a Cu2ZnSnSe4 absorber for thin-film solar cells

“…Experiments performed with the 457 nm excitation wavelength revealed the presence of ZnSe phase. Two intense bands located at 252 and 503 cm -1 belong to the resonantly enhanced ZnSe Raman band from LO phonon and first overtone, respectively [31,46]. Fig.…”

Effects of metal ion concentration on electrodeposited CuZnSn film and its application in kesterite Cu2ZnSnS4 solar cells

“…Among them, ternary alloys based on CuZnSn (CZT) were mainly employed in industries for decorative and protective purposes in early time. 6 Over recent years, it has been widely used as an essential precursor to synthesize new sustainable photovoltaic materials such as Cu 2 ZnSnS 4 (CZTS) 7-10 and Cu 2 ZnSnSe 4 (CZTSe) [11][12][13][14] . Solar cells using electrodeposited Cu 2 ZnSnS 4 (CZTS) and Cu 2 ZnSnSe 4 (CZTSe) with efficiency up to 8.0% [15][16][17][18] have been reported.…”

Микроструктура и комбинационное рассеяние света тонких пленок Cu-=SUB=-2-=/SUB=-ZnSnSe-=SUB=-4-=/SUB=-, осажденных на гибкие металлические подложки

“…Из представленных СЭМ изображений пленок CZTSe видно (рис. 1), что в зависимости от элементного состава сформирована различная морфология [17][18][19]. Обнаружено, что на поверхности пленки CZTSe на Мо-подложке сформированы мелкие и единичные круп-ные кристаллиты (рис.…”

“…Наблюдаемые светлые/яркие участки на поверхности пленок CZTSe обогащены цинком и, по-видимому, соответствуют фазе ZnSe [16]. Образо-вание фазы ZnSe на поверхности пленок согласуется с предложенной в работе [18] моделью роста пленок CZTSe, обогащенных цинком, согласно которой кристал-лы CZTSe растут крупными и образуют компактный слой, оставляя избыток цинка на поверхности, что приводит к формированию побочной фазы ZnSe.…”