Analisis Pengaruh Fraksi Berat Pengisi Komposit PANi/n-SiO2 terhadap Sifat Elektrokimia dengan Metode Polarisasi Potensiodinamik

Abstract

The study of the effect of the weight fraction of the filler on the PANi/n-SiO2 composite was carried out in a high salinity medium. Nanosilica (n-SiO2) was synthesized from amorphous silica coprecipitation of Bancar Tuban natural sand using calcination method at 900oC for 6 hours. The synthesized nanosilica was mixed with paint using a variation of filler weight 0.25; 0.5; and 0.75 grams, then coated on SS304 steel. Corrosion experiments consist of two methods, namely polarization to determine the corrosion rate and immersion to identify corrosion products. The experimental results show that the PS50 sample has the lowest rate of 1.04x10-5 mpy

Komposit polianilin/logam oksida: sintesis, karakterisasi dan aplikasi: sebuah telaah pustaka

“…Komposit PANi/SiO2 dilapiskan pada baja SS304 untuk melihat potensinya sebagai antikorosi dengan metode polarisasi untuk menentukan laju korosi dan metode pencelupan untuk mengidentifikasi produk korosi. Hasilnya menunjukkan bahwa komposit PANi/n-SiO2 berhasil menekan laju korosi baja SS304 hingga 500-2000 kali lebih kecil, dengan laju korosi PANi/n-SiO2 dengan komposisi 0,25 g, 0,50 g, dan 0,75 g berturut-turut adalah 1,31x10 -5 mpy, 1,04x10 -5 mpy, dan 4,85x10 -4 mpy [13]. Proses pelapisan cat dengan PANi dan komposit PANi/SiO2 pada permukaan baja SS304 dilakukan menggunakan metode spray coating.…”