Al₃Ti/ADC12 Composite Synthesized by Ultrasonic Chemistry in Situ Reaction

Abstract

Al3Ti/ADC12 composite was synthesized in situ using Al-fluoride potassium titanate (K2TiF6) as the reaction system and an ultrasonic assisted direct melt reaction. Results indicate ultrasonic chemistry reactions are both accelerated and more complete compared to traditional in situ reactions. Al3Ti reinforced particles with a regular shape and size of 1-2 μm were well distributed and as-cast microstructures of composites were superior. Composite particles under ultrasonic assistance were also refined to a greater extent. Tensile strength and elongation rate of the composites reached 255 MPa and 2.2%, an increase of 19.1% and 37.5% respectively to those without ultrasonic aid. Cleavage surface of the composite declined and the number of dimples increased while dimples became smaller and deeper, showing obvious ductile fracture.

In Situ Formation of ZrB2 and Its Influence on Wear and Mechanical Properties of ADC12 Alloy Mixed Matrix Composites

“…There have been few works with reinforcement of ADC12 alloys in literature. Sun et al [ 14 ] synthesized in situ Al 3 Ti/ADC12 composite using the reaction system with the ultrasonic-assisted direct melt method. The results showed that ultrasonic chemistry reactions accelerated the formation of Al 3 Ti in comparison to the traditional in situ method.…”