A Confocal Raman Imaging Study of an Optically Transparent Boron-Doped Diamond Electrode

Abstract

International audienceConfocal micro-Raman imaging was used to investigate the structural and, to some extent, the chemical inhomogeneities that exist in a high-quality, free-standing, polished, optically transparent boron-doped chemical-vapor-deposition (CVD) diamond disk. A number of boron-related Raman lines centered at about 610, 925, 1045, 1375, and 1470 cm^-1 were evidenced and found to vary from one region of the disk to another. These lines have previously been reported in the literature for other boron-doped crystals or films obtained using completely different growth conditions. Even if their origin is still somewhat uncertain, their presence enabled the construction of spatial maps of the boron signal intensity over the surface. It was confirmed that boron is incorporated into CVD diamond with significant inhomogeneities. In most cases, the boron signal intensity tracked the structure of the grains. The high quality of the disk also allowed a detailed analysis of the grain boundaries to be made. However, a unique description of these grain boundaries in terms of their microstructure and chemical composition could not be developed. There is some evidence that nondiamond phases are incorporated into the grain boundaries, but their Raman signature is quite distinct from that usually reported. Another remarkable feature of this disk is that it is nearly photoluminescence-free. Photoluminescence, as excited by the 514.5 or 457.9 nm lines of an argon ion laser, was only detected within some of the nondiamond amorphous carbon-rich grain boundaries. The low photoluminescence background was also a common feature of a heavily boron-doped, polycrystalline film deposited on silicon, another sample that was also examined in this work for comparison. Despite its high quality, the optically transparent disk is far from being stress-free. Localized stress variations were observed. The strained regions are not systematically associated with the incorporation of nondiamond carbon. Grain boundaries and, most probably, planar defects have been identified as the stress sources. However, it remains difficult to explain the large compressive stress observed for some of the crystals

Electron Transfer Kinetics of Ferrocene at Microcrystalline Boron‐Doped Diamond Electrodes: Effect of Solvent and Electrolyte

“…Given the level of asymmetry, the doping level may be estimated to be in the high 10 19 cm À3 range, consistent with the boron nuclear reaction analysis [18 ± 20]. It should be mentioned, however, that the doping level threshold for the appearance of the diamond line asymmetry varies somewhat from report to report [21].…”

The Fabrication and Characterization of a Nickel Nanoparticle Modified Boron Doped Diamond Electrode for Electrocatalysis of Primary Alcohol Oxidation

“…This is due to the boron doped nature of the polycrystalline diamond, leading to areas of increased reactivity depending on the concentration of B atoms, which are present in an approximate ratio of 1 boron atom to 1000 carbon atoms [30]. Increased activity at the diamond grain boundaries is a feature suggested by the SEM images of polished polycrystalline high quality BDD surfaces [20,31,32], and varied local reactivity has also been reported via confocal Raman imaging, photoluminescence [33] and AC impedance experiments [34,35]. As such BDD is an excellent electrode material to promote the formation of nanoparticles as opposed to films.…”

Surface Modifications of Nanodiamonds and Current Issues for Their Biomedical Applications

“…The nature of outer shells must be well characterized because it strongly affects the surface reactivity of nanodiamonds. Raman spectroscopy gives access to composition and structure for bulk carbon phases [71]. A signature at 1332 cm −1 is obtained for diamond while D and G bands at 1410 and 1590 cm −1 originate from amorphous and graphitic carbon, respectively.…”