Abstract

Recebido em 24/6/11; aceito em 27/11/11; publicado na web em 20/1/12 SURFACE ENERGY FOR (001) TiO 2 NANOSURFACES. In this work was made an investigation about bulk and surface models (at maximum 20 layers) of the TiO 2 material in the (001) direction. TiO 2 commercial sample was feature using XDR technique to determine phase and crystallites average size. Bulk and (001) surface models were simulated for TiO 2 material using DFT/B3LYP and its results were used for calculating energy surface, electronic levels, superficial atomic displacement and charge maps. Atoms of the first and second layers of the slab model showed electronic densities very well organized in the form of chains or wires.

Obtenção por electrospinning e caracterização de fibras de pentóxido de nióbio (Nb2O5)

“…O pentóxido de nióbio tem apresentado resultados promissores como fotocatalisador e vem sendo estudado como alternativa para substituir o TiO 2 por apresentar valores de gap próximos ao óxido de titânio, muito utilizado em fotocatálise, com a vantagem de ser facilmente recuperado e reciclado ao fi nal do processo. O gap maior que 3,5 eV mostra que as fi bras obtidas podem ser utilizadas para substituir o TiO 2, que apresenta valores de gap mais próximos a 3,0 eV (Lazaro et al, 2012;Silva e Lansarin, 2013;Bernardes et al, 2011), apresentando, inclusive, maior capacidade de oxidação que as fi bras de TiO 2 .…”

“…de de oxidação para as fi bras e, consequentemente, maior efi ciência de degradação durante uma reação fotocatalítica (Lazaro et al, 2012).…”