The best method of hardening of low-value wood is pressing her to the extent of 40-50 %. About 2 times its volume decreases and, respectively, but the output of the modified wood. As hardener can be used on-nofibrillyarnuyu cellulose (NFP) in the form of a 2 % hydrogel magnetically activated. Completely replace the pressing NFP is impossible, since hydrogel has a very small concentration of NFP and receive content over 1 % in relation to dry wood impossible. Technology for producing modified wood involves activation of a 2 % hydrogel magnetization in STEL-49 to obtain the analyte with a potential of 600-800 mV and the pH = 2.5. In a 30 % aqueous urea solution was added 20 % activated hydrogel NFP stabilizer and 15 % the size of the particle board - UREAFORMALDEHYDE oligomer aqueous solution (UFC). The resulting mixture is impregnated with crude wood aspen or birch end under pressure to ensure through impregnation. The content of the mixture in the impregnated wood of 40-60 % by weight of the wood. The impregnated wood is dried with simultaneous compression to the extent of 20-25 %. The resulting wood has a moisture content 6-8 %, the density of 800-900 kg / m3, compressive strength parallel to the grain of 100-150 MPa. Due to the presence of urea loss on fire test is reduced 5 times. Biostability modified wood increases from baseline in 2-3 raza.Posle processing wood according to the procedure described obtained modified wood having a degree of compaction of 15 % birch and 25 % aspen, i.e. Use of the method reduces the degree of compaction is twice as compared with the known method, thus also increasing the yield of the resulting material. Reducing pressing for birch from 30 to 15 % increases the yield of modified wood by 15 %, ie 1 m3 with savings of 0.15 m3, with 1000 m3 -150 m3, When the selling price of the modified birch 30 thousand rubles. 1 m3 for savings of 150x30 = 4500 rubles. Reducing the degree of compaction of the aspen from 50 to 25 % increases the yield of modified wood by 25 %, i.e. 1 m3 with savings of 0.25 m3, with 1000 m3 -250 m3. When the selling price of the modified aspen wood 25 thousand rubles. 1 m3 for savings of 250x25 = 6250 rubles.
Structural and anatomical models of alder wood have been developed on the basis of technical and physical models of wood. The models enable to solve the problem of penetrating changes in wood texture by combining selective treatment (impregnation) with two wood colouring agents in different directions of anisotropy, followed by uneven pressing. Specimens with the texture of mahogany, rosewood, walnut, etc have been obtained. Alder wood is pressed at an angle of 45° to the radial direction to obtain the texture of mahogany, at an angle of 90° – for a texture of rosewood. At the same time, physical and mechanical properties of modified wood correspond to similar indicators of wood of these species. The study of macro-and microstructure of pressed wood suggests that texture of the obtained material corresponds to the texture of rosewood and mahogany. It is possible to imitate any species of valuable wood using the obtained structural models and the developed techniques.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.