The potential of an ultrapermeable benzotriptycene-based polymer of intrinsic microporosity (PIM-TMN-Trip) for the upgrading of biogas is investigated. Permeation experiments were performed using an in-house bespoke permeation unit for pure gases and gas mixtures, and included tests with model mixtures as well as real biogas from a sewage treatment plant, under dry and humid conditions. Permeability and CO2/CH4 selectivity for either pure gases or for real biogas were high and lie close to or on the recently defined 2019 Robeson upper bound based on ideal permselectivities. In addition, a remarkable increase in CO2/CH4 selectivity was observed after two weeks of continuous exposure to CO2 due to a significant decrease of CH4 permeability. The constant CO2 permeability and increased selectivity upon ageing suggest that ageing in the presence of CO2 causes a rearrangement, rather than a reduction of the fractional free volume. The mixed gas permeability experiments were performed with high stage-cut in order to mimic a real separation process, and the results confirmed the potential of PIM-TMN-Trip membranes for biogas upgrading.
The last decade has seen an exponential increase in the number of studies focused on novel applications for ionic liquids (ILs). Blends of polymers with ILs have been proposed for use in fuel cells, batteries, gas separation membranes, packaging, etc., each requiring a set of specific physico-chemical properties. In this work, blends of four grades of the poly(ether-ester) multiblock copolymer PolyActive™ with different concentrations of the CO2-philic 1-butyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide [BMIM][Tf2N] were prepared in the form of dense films by a solution casting and solvent evaporation method, in view of their potential use as gas separation membranes for CO2 capture. Depending on the polymer structure, the material properties could be tailored over a wide range by means of the IL content. All samples were dry-feeling, highly elastic self-standing dense films. The microstructure of the blends was studied by scanning electron microscopy with a backscattering detector, able to observe anisotropy in the sample, while a special topographic analysis mode allowed the visualization of surface roughness. Samples with the longest poly(ethylene oxide terephthalate) (PEOT) blocks were significantly more anisotropic than those with shorter blocks, and this heterogeneity increased with increasing IL content. DSC analysis revealed a significant decrease in the melting enthalpy and melting temperature of the crystalline PEOT domains with increasing IL content, forming an amorphous phase with Tg ≈ −50 °C, whereas the polybutylene terephthalate (PBT) phase was hardly affected. This indicates better compatibility of the IL with the polyether phase than the polyester phase. Young’s modulus was highest and most IL-dependent for the sample with the highest PEOT content and PEOT block length, due to its high crystallinity. Similarly, the sample with short PEOT blocks and high PBT content also showed a high modulus and tensile strength, but much lower maximum elongation. This study provides a detailed discussion on the correlation between the morphological, thermal, and mechanical properties of these PolyActive™/[BMIM][Tf2N] blends.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.