We report here the first example of ZIF materials synthesized in aqueous solution. The synthesis was performed at room temperature and typically took several minutes compared to hours and days in non-aqueous conditions. The obtained product were ZIF-8 nanocrystals having size of ~85 nm and showed excellent thermal, hydrothermal and solvothermal stabilities.
A seeded growth method for the fabrication of high-permeance, high-separation-factor zeolite (siliceous ZSM-5, [Si96O192]-MFI) membranes is reported. The method consists of growing the crystals of an oriented seed layer to a well-intergrown film by avoiding events that lead to a loss of preferred orientation, such as twin overgrowths and random nucleation. Organic polycations are used as zeolite crystal shape modifiers to enhance relative growth rates along the desirable out-of-plane direction. The polycrystalline films are thin (approximately 1 micrometer) with single grains extending along the film thickness and with large in-plane grain size (approximately 1 micrometer). The preferred orientation is such that straight channels with an open diameter of approximately 5.5 angstroms run down the membrane thickness. Comparison with previously reported membranes shows that these microstructurally optimized films have superior performance for the separation of organic mixtures with components that have small differences in size and shape, such as xylene isomers.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.