The temperature dependence of the dc magnetization and the specific heat capacity are systematically investigated for the perovskite YbCrO3 chromites. The results show that there exist two complex sequences of magnetic transitions with the characteristics of magnetization reversal and Yb3+/Cr3+ spin ordering at different temperature, respectively. The antiferromagneticlike transition around TN=118 K is attributed to the antiferromagnetic ordering of the Cr3+ spins and a negative magnetization, accompanied with a tendency to the plateau below 10 K caused by the Yb3+ ordering. We obtain the Weiss constant of −197.0 K and an effective moment of 5.99μB for the sum of the free ion values of 4.53μB for Yb3+ and 3.87μB for high-spin Cr3+ from the experiments, which shows an antiferromagnetic interaction and the existence of weak canted antiferromagnetic (CAFM) characteristics. Corresponding to the magnetic phase transition in the Cr sublattice, the specific heat capacity under zero fields exhibits a sharp λ-shape peak near temperature TN, which is depressed and broadened smoothly with the increase in the magnetic field. And a shoulder-shaped Schottky-type anomaly below 12 K is observed in the specific heat capacity curves. This can be interpreted by accounting for the molecular field approximation by assuming that the induced polarization of the paramagnetic ytterbium ions is opposite to the ferromagnetic moment of the chromium ions. According to the results of the zero fields cooling and the field cooling magnetization, the possible existence of spin ordering for the Yb3+ moments can be predicted.
The magnetocaloric effect (MCE) is an intrinsic property of magnetic materials that enable magnetic refrigeration devices without using the traditional vapour-compression. Temperature sensitive and anisotropic magnetic solids might give rise to a large rotating MCE for building compact and efficient magnetic cooling systems by simply rotating the sample. Here, we report an unprecedented maximal refrigeration capacity of 497.36 J/kg (at 70 kOe) in perovskite TbFeO3 single crystal, resulting from its giant anisotropic magnetic entropy change along a axis. Our paper reveals that interaction between Fe-3d and Tb-4f electrons drives extremely interesting spin reorientation transition, which is highly sensitive to magnetic field and temperature. These findings highlight potential applications of an emerging material for high efficient low temperature magnetic refrigeration, which is compact and quiet, and does not use ozone-depleting coolant gases.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.