It is now more popular to use basalt fibers in the engineering programs to reinforce the crack resistance of asphalt mixtures. However, research concerning the impact of the basalt fiber diameter on the macro performance of AC-13 mixtures is very limited. Therefore, in this paper, basalt fibers with three diameters, including 7, 13 and 25 μm, were selected to research the influences of fiber diameter on the crack resistance of asphalt mixtures. Different types of crack tests, such as the low temperature trabecular bending test (LTTB), the indirect tensile asphalt cracking test (IDEAL-CT), and the semi-circular bend test (SCB), were conducted to reveal the crack resistance of AC-13 mixtures. The entire cracking process was recorded through the digital image correlation (DIC) technique, and the displacement cloud pictures, strain, average crack propagation rate (V) and fracture toughness (FT) indicators were used to evaluate the crack inhibition action of the fiber diameter on the mixture. The results showed that the incorporation of basalt fiber substantially improved the crack resistance, slowed down the increase of the displacement, and delayed the fracture time. Basalt fiber with a diameter of 7 μm presented the best enhancement capability on the crack resistance of the AC-13 mixture. The flexibility index (FI) of the SCB test showed a good correlation with V and FT values of DIC test results, respectively. These findings provide theoretical advice for the popularization and engineering application of basalt fibers in asphalt pavement.
A wide variety of polymer additives have been widely used in recent years. However, the effect of different polymer additives on the durability of asphalt binders has not been investigated thoroughly. To evaluate the aging property of styrene-butadiene-styrene (SBS) asphalt binder with different polymer additives, three polymer modifiers, namely high modulus modifier (HMM), anti-rutting agent (ARA), and high viscosity modifier (HVM), were added to it. First, the Thin Film Over Test (TFOT) and Pressure Aging Vessel (PAV) was performed on the asphalt binders. The rheological properties of the four asphalt binders before and after aging were then checked by the Dynamic Shear Rheometer Test (DSR). The chemical compositions of the asphalt binders were determined by the Fourier Transform Infrared Spectrometer (FTIR) test. Several aging indicators were adopted to reflect the aging degree of the asphalt binders. The results show that when polymer additives are added to the SBS asphalt binder, the complex modulus, storage modulus, loss modulus, and rutting factor substantially increase and the phase angle decreases. All the test parameters become higher after aging. The phase angle of the SBS asphalt binder is the highest at both unaged and aged states, while its other parameters values are the smallest. Moreover, the Carbonyl Aging Indicator (CAI) of SBS with polymer additives becomes lower under both TFOT and PAV conditions, indicating that polymer additives can improve the aging resistance of SBS asphalt, of which HVM modifies the aging resistance best. Complex Modulus Aging Indicator (CMAI) and Storage Modulus Aging Indicator (SMAI) have the best correlation coefficients with CAI, and the two aging indicators can be used to predict the aging degree of polymer modified asphalt binders.
To evaluate the long-term performances of different polymer-modified asphalt mixtures, three modifiers were chosen to modify AC-13 (defined as the asphalt concrete with the aggregate nominal maximum particle size of 13.2 mm); namely, high viscosity modifier (HVM), high modulus modifier (HMM), and anti-rutting agent (ARA). The deformation and cracking resistance of different polymer-modified mixtures were checked at different aging conditions (unaged, short-term aged, and long-term aged for 5, 10, and 15 days respectively). The results of the Hamburg wheel-track test and uniaxial penetration test (UPT) showed that the rutting resistance of all asphalt mixtures changed in a V-shape as the aging progressed. From the unaged stage to the long-term aging stage (5 days), the rutting resistance decreases gradually. While after the long-term aging stage (5 days), the rutting resistance increases gradually. Results from the semicircular bending test (SCB) and the indirect tensile asphalt cracking test (IDEAL-CT) indicated that the cracking resistance of all the mixtures gradually decline with the deepening of the aging degree, indicating that aging weakens the crack resistance of asphalt mixtures. Additionally, test results showed that the rutting resistance of ARA AC-13 (defined as AC-13 containing ARA) is the best, the cracking resistances of ARA AC-13, HMM AC-13 (defined as AC-13 containing HMM) and HVM AC-13 (defined as AC-13 containing HVM) have no significant difference, and different polymer modifiers had different sensitivities to aging due to the polymer content and the type of modifier. The conclusions of this study help to further understand the long-term performance of polymer-modified asphalt mixtures during service life and to help guide the selection of modifiers for mixtures.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.