In the present study, maleimide-modified epoxide resin containing UV-curable hybrid coating materials were prepared and coated on polycarbonate substrates in order to improve their surface properties. UV-curable, bismaleimide-modified aliphatic epoxy resin was prepared from N-(p-carboxyphenyl) maleimide (p-CPMI) and cycloaliphatic epoxy (Cyracure-6107) resin. The structure of the bismaleimide modified aliphatic epoxy resin was analyzed by FTIR and the characteristic absorption band for maleimide ring was clearly observed at 3100 cm S1 . Silica sol was prepared from tetraethylorthosilicate (TEOS) and methacryloxy propyl trimethoxysilane (MAPTMS) by sol-gel method. The coating formulations with different compositions were prepared from UV-curable bismaleimide-based epoxy oligomer and sol-gel mixture. The molecular structure of the hybrid coating material was analyzed by 29 Si-CP/ MAS NMR spectroscopy techniques. In the 29 Si CP/MAS NMR spectrum of the hybrid coating, mainly two kinds of signals were observed at S68 and S110 ppm that correspond to T 3 and Q 4 peaks, respectively. This result shows that a fully condensed structure was obtained. The thermal and morphological properties of these coatings materials were investigated by using TGA and SEM techniques. Hardness and abrasion resistance properties of coating materials were examined and both were found to increase with sol-gel precursor content of the coating. The photopolymerization kinetics was investigated by using RT-IR. 70% conversion was attained with the addition of 15 wt% of BMI resin into the acrylate-based coating formulation. It was found that the UV-curable organic-inorganic hybrid coatings improved the surface properties of polycarbonate.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.