Nickel ferrite (NixFe3-xO4) have been synthesized using solid state reaction with composition (2x)NiO : (3-x)Fe2O3 (x = 0.5; 1.0; 1.5 dan 2.0) in mol in wt%. Mixing of this powder was milled with HEM (High Energy Milling) for 10 hours, and then sintered at 1000 °C for 3 h. X-ray diffraction pattern indicates that the all of samples are single phase in this stage. FTIR (Fourier transform infrared) analysis showed two absorption bands in the range of ~410 - ~600 cm-1 related to octahedral and tetrahedral sites. The magnetic measurement using vibrating sample magnetometer (VSM) shows that the sample exhibited a ferromagnetic behaviour with its coercivity value in the range of 164-217 Oe, and the maximum value wasshowed by x =1.5. VNA (Vector Network Analyzer) characterization shows the ability electromagnetic wave absorption with RL (reflection loss) value of -28 dB occurs at frequency of 10.98 GHz. It means that the Ni1.5Fe1.5O4 sample can absorb microwave about ~96 % at 10.98 GHz.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.