Black titania nanotube arrays are prepared for the first time, which exhibit an excellent photoelectrochemical water-splitting performance.

Hydrogenated black titania, with a crystalline core/amorphous shell structure, has attracted global interest due to its excellent photocatalytic properties. However, the understanding of its structure-property relationships remains a great challenge and a more effective method to produce hydrogenated titania is desirable. Herein, we report a TiH2 assisted reduction method to synthesize bluish hydrogenated titania (TiO2-x:H) that is highly crystallized. The characteristic amorphous shells, which are essential for the enhancement of solar absorption and photocatalysis in many reported hydrogenated titania, are completely removed by hydrogen peroxide. The blue TiO2-x:H sample without amorphous shells delivers not only significantly improved visible- and infrared-light absorption but also greatly enhanced photocatalytic activity compared to pristine TiO2. Its water decontamination is 2.5 times faster and the hydrogen production was 1.9-fold higher over pristine TiO2. Photoelectrochemical measurement reveals greatly improved carrier density and photocurrent (a 4.3-fold increase) in the reduced TiO2-x:H samples. This work develops a facile and versatile method to prepare hydrogenated titania and proposes a new understanding of the hydrogenated titania that doped hydrogen atoms, instead of the amorphous shells, are essential for its high photocatalytic performance.

Hierarchical branched nanoparticles are one promising nanostructure with three-dimensional open porous structure composed of integrated branches for superior catalysis. We have successfully synthesized Pt-Cu hierarchical branched nanoparticles (HBNDs) with small size of about 30 nm and composed of integrated ultrathin branches by using a modified polyol process with introduction of poly(vinylpyrrolidone) and HCl. This strategy is expected to be a general strategy to prepare various metallic nanostructures for catalysis. Because of the special open porous structure, the as-prepared Pt-Cu HBNDs exhibit greatly enhanced specific activity toward the methanol oxidation reaction as much as 2.5 and 1.7 times compared with that of the commercial Pt-Ru and Pt-Ru/C catalysts, respectively. Therefore, they are potentially applicable as electrocatalysts for direct methanol fuel cells.