To prepare ultra-fine particles and offer correlative applications such as the micronization of drugs with rapid expansion of supercritical solution (RESS), the first work in measuring the solubility of risocaine has been carried out at different operation conditions in this paper. The trend of solubility due to changes in specific operational parameters has been examined. The results of pressure (9-30 MPa) and temperature (308-328K) effecting on solubility show that the solubility increases mainly along with the increasing density. With applying different models to correlate the solubility data, we found Chrastil models had better correlation effects than the Peng Robinson EOS model, Mendez-Santiago and Teja equation model, with providing a nearly perfect average absolute relative deviation (AARD) of 0.0596. In the second part of work, RESS was applied to prepare risocaine particles at five different process conditions, including extraction temperature (308-328K), extraction pressure (9-30MPa), nozzle temperature (100-120°C), nozzle diameter (0.1-0.4nm) and spray distance (2-4cm).The size and morphology were determined by scanning electron microscopy (SEM). On the basis of the different experimental operation conditions, granular, filmily and threadlike particles with diameter (1-100nm) were obtained, it was also demonstrated that a successful size reduction of risocaine particles.
This paper researched the inorganic coated the rutile titanium dioxide process, a new inorganic coating (The rutile titanium dioxide ternary Inorganic coated were prepared by sol-gel method). The regression equation and the optimum conditions are founded by uniform design and the systemetical research of various factors on the properties of the rutile titanium dioxide ternary Inorganic Coated. Effect of The rutile titanium dioxide ternary Inorganic coated were characterized by nanoZS, Fourier infrared spectroscopic analysis (FT-IR) with NH3 as atom probe, scanning electron microscopy (SEM), transmission electron microscopy (TEM). The optimized formula of preparing the rutile titanium dioxide ternary inorganic coated is that the dispersant of 0.20%, the ZrO2 content of 0.6%, the SiO2 content of 3.0%, the Al2O3 content of 1.6%, the rotate speed of 340r/min when system temperature was 60°C-65°C, the seriflux concentration was 300g/L, the PH of the coated ZrO2 was 8.5-9.0, the PH of the coated SiO2 was 9.5-10.0, the PH of the coated Al2O3 was 6.0-6.5.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.